Stainless Steel S82122 Annealed vs S82122 CW 1/4H
Stainless Steel · S82122 temper comparison
S82122 Annealed and S82122 CW 1/4H are two conditions of the same stainless steel grade, S82122: Annealed versus CW 1/4H (cold worked strip/tube, quarter-hard temper). The chemistry is identical, so every difference below comes from the condition. S82122 CW 1/4H is the stronger of the two: yield strength 750 MPa (109 ksi) against 520 MPa (75.4 ksi) for S82122 Annealed, about 44% more; tensile strength follows at 900 MPa (131 ksi) vs 720 MPa (104 ksi). In exchange, S82122 Annealed is the more ductile: elongation 30% versus 12% for S82122 CW 1/4H, and S82122 CW 1/4H is harder (300 HB vs 240 HB). S82122 Annealed runs hotter in service (300°C vs 250°C continuous).
S82122 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
S82122 CW 1/4HChoose it when strength drives the design.
S82122 Annealed vs S82122 CW 1/4H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 148 GPa21.5 Msi · Poisson's Ratio 0.3 · Hardness, Rockwell B 99 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.75 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,455°C2,651 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 15 W/m·K8.7 BTU/hr·ft·°F · Specific Heat Capacity 480 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 13 µm/m·K7.2 µin/in·°F · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 8×10⁻⁷ Ω·m31.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.15 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 53 MJ/kg22,786 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 180 L/kg21.6 gal/lb · Typical Recycled Content 65%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
S82122 Annealed vs S82122 CW 1/4H — frequently asked
Is S82122 CW 1/4H stronger than S82122 Annealed?
Yes. S82122 CW 1/4H has a typical yield strength of 750 MPa (109 ksi) against 520 MPa (75.4 ksi) for S82122 Annealed — about 44% more. Tensile strength is 900 MPa (131 ksi) vs 720 MPa (104 ksi).
Which condition does FabDigit quote by default, Annealed or CW 1/4H?
Annealed is the default S82122 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, S82122 Annealed or S82122 CW 1/4H?
S82122 Annealed, by a small margin. Both rate poor for machinability — 33/100 against 27/100 for S82122 CW 1/4H; for welding the order is S82122 Annealed first (very good, 70/100) then S82122 CW 1/4H (good, 62/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in S82122 Annealed and S82122 CW 1/4H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.