Stainless Steel S44537 Annealed vs S44537-TR
Stainless Steel · S44537 temper comparison
S44537 Annealed and S44537-TR are two conditions of the same stainless steel grade, S44537: Annealed versus TR (temper rolled / skin passed). The chemistry is identical, so every difference below comes from the condition. S44537-TR is the stronger of the two: yield strength 450 MPa (65.3 ksi) against 350 MPa (50.8 ksi) for S44537 Annealed, about 29% more; tensile strength follows at 560 MPa (81.2 ksi) vs 510 MPa (74 ksi). In exchange, S44537 Annealed is the more ductile: elongation 24% versus 15% for S44537-TR, and S44537-TR is harder (200 HB vs 175 HB).
S44537 AnnealedChoose it when the part is bent, formed or impact-loaded.
S44537-TRChoose it when strength drives the design.
S44537 Annealed vs S44537-TR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 158 GPa22.9 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 20.5 W/m·K11.8 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 260 J/g112 BTU/lb · Max Service Temperature (continuous) 1,000°C1,832 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.6 % IACS · Electrical Resistivity 6.7×10⁻⁷ Ω·m26.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.15 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 50 MJ/kg21,496 BTU/lb · Embodied Carbon (primary production) 4 kg CO₂/kg · Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 65%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
S44537 Annealed vs S44537-TR — frequently asked
Is S44537-TR stronger than S44537 Annealed?
Yes. S44537-TR has a typical yield strength of 450 MPa (65.3 ksi) against 350 MPa (50.8 ksi) for S44537 Annealed — about 29% more. Tensile strength is 560 MPa (81.2 ksi) vs 510 MPa (74 ksi).
Which condition does FabDigit quote by default, Annealed or TR?
Annealed is the default S44537 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose S44537 Annealed over S44537-TR?
Pick S44537 Annealed when the part is bent, formed or impact-loaded. Pick S44537-TR when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in S44537 Annealed and S44537-TR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.