Stainless Steel S41045 1/2H vs S41045 N+T
Stainless Steel · S41045 temper comparison
S41045 1/2H and S41045 N+T are two conditions of the same stainless steel grade, S41045: 1/2H (half hard) versus N+T (normalized and tempered). The chemistry is identical, so every difference below comes from the condition. S41045 1/2H is the stronger of the two: yield strength 550 MPa (79.8 ksi) against 360 MPa (52.2 ksi) for S41045 N+T, about 53% more; tensile strength follows at 620 MPa (89.9 ksi) vs 550 MPa (79.8 ksi). In exchange, S41045 N+T is the more ductile: elongation 22% versus 8% for S41045 1/2H, and S41045 1/2H is harder (220 HB vs 190 HB). S41045 N+T runs hotter in service (650°C vs 480°C continuous).
S41045 1/2HChoose it when strength drives the design.
S41045 N+TChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
S41045 1/2H vs S41045 N+T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,480°C2,696 °F · Liquidus Temperature 1,530°C2,786 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 25 W/m·K14.4 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3 % IACS · Electrical Resistivity 5.7×10⁻⁷ Ω·m22.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V · Corrosion Resistance 42 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 33 MJ/kg14,187 BTU/lb · Embodied Carbon (primary production) 2.9 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 65%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
S41045 1/2H vs S41045 N+T — frequently asked
Is S41045 1/2H stronger than S41045 N+T?
Yes. S41045 1/2H has a typical yield strength of 550 MPa (79.8 ksi) against 360 MPa (52.2 ksi) for S41045 N+T — about 53% more. Tensile strength is 620 MPa (89.9 ksi) vs 550 MPa (79.8 ksi).
Which condition does FabDigit quote by default, 1/2H or N+T?
Annealed is the default S41045 condition in the FabDigit quote flow (neither 1/2H nor N+T). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, S41045 1/2H or S41045 N+T?
S41045 N+T, by a small margin. Both rate fair for machinability — 50/100 against 45/100 for S41045 1/2H; for welding the order is S41045 N+T first (good, 68/100) then S41045 1/2H (good, 62/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in S41045 1/2H and S41045 N+T side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.