Stainless Steel S21904 Annealed vs S21904-CD
Stainless Steel · S21904 temper comparison
S21904 Annealed and S21904-CD are two conditions of the same stainless steel grade, S21904: Annealed versus CD (cold drawn). The chemistry is identical, so every difference below comes from the condition. S21904-CD is the stronger of the two: yield strength 690 MPa (100 ksi) against 415 MPa (60.2 ksi) for S21904 Annealed, about 66% more; tensile strength follows at 900 MPa (131 ksi) vs 745 MPa (108 ksi). In exchange, S21904 Annealed is the more ductile: elongation 48% versus 25% for S21904-CD, and S21904-CD is harder (285 HB vs 200 HB). S21904 Annealed runs hotter in service (760°C vs 425°C continuous).
S21904 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
S21904-CDChoose it when strength drives the design.
S21904 Annealed vs S21904-CD: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 420 MPa60.9 ksi · Shear Strength 480 MPa69.6 ksi · Fracture Toughness (K_IC) 200 MPa·√m182 ksi·√in · Hardness, Rockwell B 95 HRB · Hardness, Vickers 210 HV
Physical
Density and transition temperatures.
Same in both: Density 7.83 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,370°C2,498 °F · Liquidus Temperature 1,425°C2,597 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 14.5 W/m·K8.4 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 15.1 µm/m·K8.4 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -253°C-423 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.4 % IACS · Electrical Resistivity 7.2×10⁻⁷ Ω·m28.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 56 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 35 / 100 · Brazeability / Solderability 55 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 5.4 kg CO₂/kg · Embodied Water 190 L/kg22.8 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
S21904 Annealed vs S21904-CD — frequently asked
Is S21904-CD stronger than S21904 Annealed?
Yes. S21904-CD has a typical yield strength of 690 MPa (100 ksi) against 415 MPa (60.2 ksi) for S21904 Annealed — about 66% more. Tensile strength is 900 MPa (131 ksi) vs 745 MPa (108 ksi).
Which condition does FabDigit quote by default, Annealed or CD?
Annealed is the default S21904 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, S21904 Annealed or S21904-CD?
S21904-CD. Its machinability rates fair (35/100) against poor (30/100) for S21904 Annealed; for welding the order is S21904 Annealed first (very good, 78/100) then S21904-CD (very good, 70/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in S21904 Annealed and S21904-CD side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.