Stainless Steel F6b-ANN vs F6b-QT
Stainless Steel · F6b temper comparison
F6b-ANN and F6b-QT are two conditions of the same stainless steel grade, F6b: ANN (annealed) versus QT (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. F6b-QT is the stronger of the two: yield strength 660 MPa (95.7 ksi) against 320 MPa (46.4 ksi) for F6b-ANN, about 106% more; tensile strength follows at 810 MPa (117 ksi) vs 540 MPa (78.3 ksi). In exchange, F6b-ANN is the more ductile: elongation 28% versus 20% for F6b-QT, and F6b-QT is harder (265 HB vs 175 HB).
F6b-ANNChoose it when the part is bent, formed or impact-loaded.
F6b-QTChoose it when strength drives the design.
F6b-ANN vs F6b-QT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28 · Compressive Strength 660 MPa95.7 ksi · Shear Strength 490 MPa71.1 ksi · Fracture Toughness (K_IC) 75 MPa·√m68.3 ksi·√in · Hardness, Rockwell C 26 HRC · Hardness, Vickers 280 HV
Physical
Density and transition temperatures.
Same in both: Density 7.75 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,480°C2,696 °F · Liquidus Temperature 1,530°C2,786 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 24.9 W/m·K14.4 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 9.9 µm/m·K5.5 µin/in·°F · Latent Heat of Fusion 260 J/g112 BTU/lb · Max Service Temperature (continuous) 480°C896 °F · Min Service Temperature -29°C-20 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3 % IACS · Electrical Resistivity 5.7×10⁻⁷ Ω·m22.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.32 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 35 / 100 · Brazeability / Solderability 45 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 46 MJ/kg19,776 BTU/lb · Embodied Carbon (primary production) 3.4 kg CO₂/kg · Embodied Water 120 L/kg14.4 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
F6b-ANN vs F6b-QT — frequently asked
Is F6b-QT stronger than F6b-ANN?
Yes. F6b-QT has a typical yield strength of 660 MPa (95.7 ksi) against 320 MPa (46.4 ksi) for F6b-ANN — about 106% more. Tensile strength is 810 MPa (117 ksi) vs 540 MPa (78.3 ksi).
Which condition does FabDigit quote by default, ANN or QT?
QT is the default F6b condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, F6b-ANN or F6b-QT?
F6b-ANN, by a small margin. Both rate fair for machinability — 50/100 against 42/100 for F6b-QT.