Stainless Steel AUS-8 Annealed vs AUS-8 QT57-59HRC
Stainless Steel · AUS-8 temper comparison
AUS-8 Annealed and AUS-8 QT57-59HRC are two conditions of the same stainless steel grade, AUS-8: Annealed versus QT57-59HRC. The chemistry is identical, so every difference below comes from the condition. AUS-8 QT57-59HRC is the stronger of the two: yield strength 1,750 MPa (254 ksi) against 450 MPa (65.3 ksi) for AUS-8 Annealed, about 3.9 times as much; tensile strength follows at 2,050 MPa (297 ksi) vs 760 MPa (110 ksi). In exchange, AUS-8 Annealed is the more ductile: elongation 18% versus 2% for AUS-8 QT57-59HRC, and AUS-8 QT57-59HRC is harder (665 HV vs 235 HV). AUS-8 Annealed runs hotter in service (400°C vs 180°C continuous). On the shop floor, AUS-8 Annealed machines more easily (fair vs not recommended).
AUS-8 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
AUS-8 QT57-59HRCChoose it when strength drives the design.
AUS-8 Annealed vs AUS-8 QT57-59HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
AUS-8 AnnealedAUS-8 QT57-59HRC
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Reduction in Area 40% · Hardness, Brinell 225 HB · Hardness, Rockwell B 97 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.75 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 24 W/m·K13.9 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.4 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3 % IACS · Electrical Resistivity 5.5×10⁻⁷ Ω·m21.7 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.35 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Polishability
Same in both: Weldability 20 / 100 · Formability (cold) 35 / 100 · Castability 25 / 100 · Brazeability / Solderability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 53 MJ/kg22,786 BTU/lb · Embodied Carbon (primary production) 5 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
AUS-8 Annealed vs AUS-8 QT57-59HRC — frequently asked
Is AUS-8 QT57-59HRC stronger than AUS-8 Annealed?
Yes. AUS-8 QT57-59HRC has a typical yield strength of 1,750 MPa (254 ksi) against 450 MPa (65.3 ksi) for AUS-8 Annealed — about 3.9 times as much. Tensile strength is 2,050 MPa (297 ksi) vs 760 MPa (110 ksi).
Which condition does FabDigit quote by default, Annealed or QT57-59HRC?
Annealed is the default AUS-8 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, AUS-8 Annealed or AUS-8 QT57-59HRC?
AUS-8 Annealed. Its machinability rates fair (40/100) against not recommended (6/100) for AUS-8 QT57-59HRC.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AUS-8 Annealed and AUS-8 QT57-59HRC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.