Stainless Steel AM-350-A vs AM-350-CRT
Stainless Steel · AM-350 temper comparison
AM-350-A and AM-350-CRT are two conditions of the same stainless steel grade, AM-350: A (solution annealed) versus CRT (cold rolled (≈50–60 % reduction) and tempered 455 °C, strip only). The chemistry is identical, so every difference below comes from the condition. AM-350-CRT is the stronger of the two: yield strength 1,550 MPa (225 ksi) against 390 MPa (56.6 ksi) for AM-350-A, about 4.0 times as much; tensile strength follows at 1,720 MPa (249 ksi) vs 1,100 MPa (160 ksi). In exchange, AM-350-A is the more ductile: elongation 40% versus 4% for AM-350-CRT, and AM-350-CRT is harder (510 HV vs 215 HV). On the shop floor, AM-350-A machines more easily (fair vs poor) and AM-350-A welds better (good vs poor).
AM-350-AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
AM-350-CRTChoose it when strength drives the design.
AM-350-A vs AM-350-CRT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Fatigue Strength (Endurance Limit)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Reduction in Area 55% · Compressive Strength 400 MPa58 ksi · Shear Strength 690 MPa100 ksi · Charpy V-Notch Impact (RT) 110 J81.1 ft·lbf · Hardness, Brinell 210 HB · Hardness, Rockwell B 95 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.69 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 16 W/m·K9.2 BTU/hr·ft·°F · Specific Heat Capacity 480 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 8×10⁻⁷ Ω·m31.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 35% · Brazeability / Solderability 50 / 100 · Polishability 72 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 4.6 kg CO₂/kg · Embodied Water 220 L/kg26.4 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
AM-350-A vs AM-350-CRT — frequently asked
Is AM-350-CRT stronger than AM-350-A?
Yes. AM-350-CRT has a typical yield strength of 1,550 MPa (225 ksi) against 390 MPa (56.6 ksi) for AM-350-A — about 4.0 times as much. Tensile strength is 1,720 MPa (249 ksi) vs 1,100 MPa (160 ksi).
Which condition does FabDigit quote by default, A or CRT?
A is the default AM-350 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, AM-350-A or AM-350-CRT?
AM-350-A. Its machinability rates fair (38/100) against poor (18/100) for AM-350-CRT; for welding the order is AM-350-A first (good, 65/100) then AM-350-CRT (poor, 25/100).