Stainless Steel 9Cr18MoV-QT52 vs 9Cr18MoV-QT60
Stainless Steel · 9Cr18MoV temper comparison
9Cr18MoV-QT52 and 9Cr18MoV-QT60 are two conditions of the same stainless steel grade, 9Cr18MoV: QT52 (Q&T 50–55 HRC) versus QT60 (Q&T 58–61 HRC). The chemistry is identical, so every difference below comes from the condition. 9Cr18MoV-QT60 is the stronger of the two: yield strength 1,750 MPa (254 ksi) against 1,500 MPa (218 ksi) for 9Cr18MoV-QT52, about 17% more; tensile strength follows at 2,000 MPa (290 ksi) vs 1,750 MPa (254 ksi). In exchange, 9Cr18MoV-QT52 is the more ductile: elongation 4% versus 2% for 9Cr18MoV-QT60, and 9Cr18MoV-QT60 is harder (690 HV vs 570 HV). 9Cr18MoV-QT52 runs hotter in service (250°C vs 150°C continuous).
9Cr18MoV-QT52Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
9Cr18MoV-QT60Choose it when strength drives the design.
9Cr18MoV-QT52 vs 9Cr18MoV-QT60: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28 · Hardness, Brinell 225 HB · Hardness, Rockwell B 98 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 24 W/m·K13.9 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.2 µm/m·K5.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 40% · Weldability 12 / 100 · Formability (cold) 30 / 100 · Brazeability / Solderability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 53 MJ/kg22,786 BTU/lb · Embodied Carbon (primary production) 4.8 kg CO₂/kg · Embodied Water 120 L/kg14.4 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
9Cr18MoV-QT52 vs 9Cr18MoV-QT60 — frequently asked
Is 9Cr18MoV-QT60 stronger than 9Cr18MoV-QT52?
Yes. 9Cr18MoV-QT60 has a typical yield strength of 1,750 MPa (254 ksi) against 1,500 MPa (218 ksi) for 9Cr18MoV-QT52 — about 17% more. Tensile strength is 2,000 MPa (290 ksi) vs 1,750 MPa (254 ksi).
Which condition does FabDigit quote by default, QT52 or QT60?
A is the default 9Cr18MoV condition in the FabDigit quote flow (neither QT52 nor QT60). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 9Cr18MoV-QT52 or 9Cr18MoV-QT60?
9Cr18MoV-QT52, by a small margin. Both rate not recommended for machinability — 10/100 against 5/100 for 9Cr18MoV-QT60.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 9Cr18MoV-QT52 and 9Cr18MoV-QT60 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.