Stainless Steel 4Cr13 Annealed vs 4Cr13-CD
Stainless Steel · 4Cr13 temper comparison
4Cr13 Annealed and 4Cr13-CD are two conditions of the same stainless steel grade, 4Cr13: Annealed versus CD (cold drawn). The chemistry is identical, so every difference below comes from the condition. 4Cr13-CD is the stronger of the two: yield strength 600 MPa (87 ksi) against 380 MPa (55.1 ksi) for 4Cr13 Annealed, about 58% more; tensile strength follows at 790 MPa (115 ksi) vs 700 MPa (102 ksi). In exchange, 4Cr13 Annealed is the more ductile: elongation 22% versus 12% for 4Cr13-CD, and 4Cr13-CD is harder (245 HB vs 217 HB).
4Cr13 AnnealedChoose it when the part is bent, formed or impact-loaded.
4Cr13-CDChoose it when strength drives the design.
4Cr13 Annealed vs 4Cr13-CD: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28 · Compressive Strength 400 MPa58 ksi · Shear Strength 430 MPa62.4 ksi · Fracture Toughness (K_IC) 60 MPa·√m54.6 ksi·√in · Charpy V-Notch Impact (RT) 35 J25.8 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 7.75 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 24.9 W/m·K14.4 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.3 µm/m·K5.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 500°C932 °F · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3.1 % IACS · Electrical Resistivity 5.5×10⁻⁷ Ω·m21.7 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V · Corrosion Resistance 42 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 30 / 100 · Brazeability / Solderability 40 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 46 MJ/kg19,776 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 80 L/kg9.6 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
4Cr13 Annealed vs 4Cr13-CD — frequently asked
Is 4Cr13-CD stronger than 4Cr13 Annealed?
Yes. 4Cr13-CD has a typical yield strength of 600 MPa (87 ksi) against 380 MPa (55.1 ksi) for 4Cr13 Annealed — about 58% more. Tensile strength is 790 MPa (115 ksi) vs 700 MPa (102 ksi).
Which condition does FabDigit quote by default, Annealed or CD?
Annealed is the default 4Cr13 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 4Cr13 Annealed or 4Cr13-CD?
4Cr13-CD, by a small margin. Both rate fair for machinability — 50/100 against 45/100 for 4Cr13 Annealed.