Stainless Steel 420J1 Annealed vs 420J1 Hot Rolled
Stainless Steel · 420J1 temper comparison
420J1 Annealed and 420J1 Hot Rolled are two conditions of the same stainless steel grade, 420J1: Annealed versus Hot Rolled. The chemistry is identical, so every difference below comes from the condition. 420J1 Hot Rolled is the stronger of the two: yield strength 500 MPa (72.5 ksi) against 440 MPa (63.8 ksi) for 420J1 Annealed, about 14% more; tensile strength follows at 800 MPa (116 ksi) vs 700 MPa (102 ksi). In exchange, 420J1 Annealed is the more ductile: elongation 22% versus 16% for 420J1 Hot Rolled, and 420J1 Hot Rolled is harder (240 HB vs 195 HB). 420J1 Annealed runs hotter in service (600°C vs 550°C continuous).
420J1 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
420J1 Hot RolledChoose it when strength drives the design.
420J1 Annealed vs 420J1 Hot Rolled: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
420J1 Annealed420J1 Hot Rolled
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,450°C2,642 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 30 W/m·K17.3 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3.1 % IACS · Electrical Resistivity 5.5×10⁻⁷ Ω·m21.7 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 35 / 100 · Castability 45 / 100 · Brazeability / Solderability 50 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 42 MJ/kg18,057 BTU/lb · Embodied Carbon (primary production) 3 kg CO₂/kg · Embodied Water 100 L/kg12 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
420J1 Annealed vs 420J1 Hot Rolled — frequently asked
Is 420J1 Hot Rolled stronger than 420J1 Annealed?
Yes. 420J1 Hot Rolled has a typical yield strength of 500 MPa (72.5 ksi) against 440 MPa (63.8 ksi) for 420J1 Annealed — about 14% more. Tensile strength is 800 MPa (116 ksi) vs 700 MPa (102 ksi).
Which condition does FabDigit quote by default, Annealed or Hot Rolled?
Annealed is the default 420J1 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 420J1 Annealed or 420J1 Hot Rolled?
420J1 Annealed, by a small margin. Both rate fair for machinability — 48/100 against 42/100 for 420J1 Hot Rolled.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 420J1 Annealed and 420J1 Hot Rolled side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.