Stainless Steel 348 1/2H vs 348-HR
Stainless Steel · 348 temper comparison
348 1/2H and 348-HR are two conditions of the same stainless steel grade, 348: 1/2H (half hard) versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. 348 1/2H is the stronger of the two: yield strength 790 MPa (115 ksi) against 245 MPa (35.5 ksi) for 348-HR, about 3.2 times as much; tensile strength follows at 1,070 MPa (155 ksi) vs 600 MPa (87 ksi). In exchange, 348-HR is the more ductile: elongation 45% versus 10% for 348 1/2H, and 348 1/2H is harder (300 HB vs 165 HB). 348-HR runs hotter in service (870°C vs 425°C continuous). On the shop floor, 348-HR welds better (excellent vs very good).
348 1/2HChoose it when strength drives the design.
348-HRChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
348 1/2H vs 348-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 193 GPa28 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.96 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,430°C2,606 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 16.3 W/m·K9.4 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.6 µm/m·K9.2 µin/in·°F · Latent Heat of Fusion 285 J/g123 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 45 / 100 · Brazeability / Solderability 65 / 100 · Polishability 78 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 53 MJ/kg22,786 BTU/lb · Embodied Carbon (primary production) 5.4 kg CO₂/kg · Embodied Water 150 L/kg18 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
348 1/2H vs 348-HR — frequently asked
Is 348 1/2H stronger than 348-HR?
Yes. 348 1/2H has a typical yield strength of 790 MPa (115 ksi) against 245 MPa (35.5 ksi) for 348-HR — about 3.2 times as much. Tensile strength is 1,070 MPa (155 ksi) vs 600 MPa (87 ksi).
Which condition does FabDigit quote by default, 1/2H or HR?
Annealed is the default 348 condition in the FabDigit quote flow (neither 1/2H nor HR). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 348 1/2H or 348-HR?
348 1/2H, by a small margin. Both rate fair for machinability — 42/100 against 36/100 for 348-HR; for welding the order is 348-HR first (excellent, 85/100) then 348 1/2H (very good, 75/100).