Stainless Steel 317-1/4 Hard vs 317 Annealed
Stainless Steel · 317 temper comparison
317-1/4 Hard and 317 Annealed are two conditions of the same stainless steel grade, 317: 1/4 Hard (quarter hard) versus Annealed. The chemistry is identical, so every difference below comes from the condition. 317-1/4 Hard is the stronger of the two: yield strength 515 MPa (74.7 ksi) against 275 MPa (39.9 ksi) for 317 Annealed, about 87% more; tensile strength follows at 860 MPa (125 ksi) vs 600 MPa (87 ksi). In exchange, 317 Annealed is the more ductile: elongation 50% versus 20% for 317-1/4 Hard, and 317-1/4 Hard is harder (250 HB vs 155 HB). 317 Annealed runs hotter in service (870°C vs 425°C continuous).
317-1/4 HardChoose it when strength drives the design.
317 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
317-1/4 Hard vs 317 Annealed: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 145 GPa21 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.98 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,375°C2,507 °F · Liquidus Temperature 1,400°C2,552 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 14.4 W/m·K8.3 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.5 µm/m·K9.2 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.3 % IACS · Electrical Resistivity 7.4×10⁻⁷ Ω·m29.1 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 78 MJ/kg33,534 BTU/lb · Embodied Carbon (primary production) 5.2 kg CO₂/kg · Embodied Water 190 L/kg22.8 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
317-1/4 Hard vs 317 Annealed — frequently asked
Is 317-1/4 Hard stronger than 317 Annealed?
Yes. 317-1/4 Hard has a typical yield strength of 515 MPa (74.7 ksi) against 275 MPa (39.9 ksi) for 317 Annealed — about 87% more. Tensile strength is 860 MPa (125 ksi) vs 600 MPa (87 ksi).
Which condition does FabDigit quote by default, 1/4 Hard or Annealed?
Solution Annealed is the default 317 condition in the FabDigit quote flow (neither 1/4 Hard nor Annealed). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, 317-1/4 Hard or 317 Annealed?
317 Annealed. Its weldability rates very good (78/100) against very good (70/100) for 317-1/4 Hard.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 317-1/4 Hard and 317 Annealed side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.