Stainless Steel 309S Cold Drawn vs 309S Hot Rolled Annealed
Stainless Steel · 309S temper comparison
309S Cold Drawn and 309S Hot Rolled Annealed are two conditions of the same stainless steel grade, 309S: Cold Drawn versus Hot Rolled Annealed (hot Rolled, Annealed and Pickled plate). The chemistry is identical, so every difference below comes from the condition. 309S Cold Drawn is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 275 MPa (39.9 ksi) for 309S Hot Rolled Annealed, about 75% more; tensile strength follows at 700 MPa (102 ksi) vs 560 MPa (81.2 ksi). In exchange, 309S Hot Rolled Annealed is the more ductile: elongation 45% versus 25% for 309S Cold Drawn, and 309S Cold Drawn is harder (220 HB vs 160 HB). 309S Hot Rolled Annealed runs hotter in service (1,000°C vs 900°C continuous).
309S Cold DrawnChoose it when strength drives the design.
309S Hot Rolled AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
309S Cold Drawn vs 309S Hot Rolled Annealed: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
309S Cold Drawn309S Hot Rolled Annealed
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Fracture Toughness (K_IC) 200 MPa·√m182 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 7.9 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 15.5 W/m·K9 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 15 µm/m·K8.3 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 7.8×10⁻⁷ Ω·m30.7 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Polishability
Same in both: Weldability 80 / 100 · Brazeability / Solderability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 62 MJ/kg26,655 BTU/lb · Embodied Carbon (primary production) 4.6 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
309S Cold Drawn vs 309S Hot Rolled Annealed — frequently asked
Is 309S Cold Drawn stronger than 309S Hot Rolled Annealed?
Yes. 309S Cold Drawn has a typical yield strength of 480 MPa (69.6 ksi) against 275 MPa (39.9 ksi) for 309S Hot Rolled Annealed — about 75% more. Tensile strength is 700 MPa (102 ksi) vs 560 MPa (81.2 ksi).
Which condition does FabDigit quote by default, Cold Drawn or Hot Rolled Annealed?
Solution Annealed is the default 309S condition in the FabDigit quote flow (neither Cold Drawn nor Hot Rolled Annealed). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 309S Cold Drawn or 309S Hot Rolled Annealed?
309S Cold Drawn, by a small margin. Both rate fair for machinability — 45/100 against 38/100 for 309S Hot Rolled Annealed.