Stainless Steel 301LN 1/2H vs 301LN-ANN
Stainless Steel · 301LN temper comparison
301LN 1/2H and 301LN-ANN are two conditions of the same stainless steel grade, 301LN: 1/2H (half hard) versus ANN (annealed). The chemistry is identical, so every difference below comes from the condition. 301LN 1/2H is the stronger of the two: yield strength 950 MPa (138 ksi) against 400 MPa (58 ksi) for 301LN-ANN, about 138% more; tensile strength follows at 1,200 MPa (174 ksi) vs 750 MPa (109 ksi). In exchange, 301LN-ANN is the more ductile: elongation 50% versus 16% for 301LN 1/2H, and 301LN 1/2H is harder (390 HV vs 230 HV). 301LN-ANN runs hotter in service (760°C vs 300°C continuous). On the shop floor, 301LN-ANN welds better (very good vs good).
301LN 1/2HChoose it when strength drives the design.
301LN-ANNChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
301LN 1/2H vs 301LN-ANN: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 145 GPa21 Msi · Poisson's Ratio 0.28 · Reduction in Area 65% · Shear Strength 460 MPa66.7 ksi · Fracture Toughness (K_IC) 160 MPa·√m146 ksi·√in · Hardness, Brinell 215 HB · Hardness, Rockwell B 88 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.9 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 15 W/m·K8.7 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16 µm/m·K8.9 µin/in·°F · Latent Heat of Fusion 280 J/g120 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.4 % IACS · Electrical Resistivity 7.3×10⁻⁷ Ω·m28.7 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V · Corrosion Resistance 56 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 65 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 53 MJ/kg22,786 BTU/lb · Embodied Carbon (primary production) 4.3 kg CO₂/kg · Embodied Water 120 L/kg14.4 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
301LN 1/2H vs 301LN-ANN — frequently asked
Is 301LN 1/2H stronger than 301LN-ANN?
Yes. 301LN 1/2H has a typical yield strength of 950 MPa (138 ksi) against 400 MPa (58 ksi) for 301LN-ANN — about 138% more. Tensile strength is 1,200 MPa (174 ksi) vs 750 MPa (109 ksi).
Which condition does FabDigit quote by default, 1/2H or ANN?
ANN is the default 301LN condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 301LN 1/2H or 301LN-ANN?
301LN-ANN. Its machinability rates fair (38/100) against poor (30/100) for 301LN 1/2H; for welding the order is 301LN-ANN first (very good, 80/100) then 301LN 1/2H (good, 65/100).