Stainless Steel 1.4941 1/4H vs 1.4941-AW
Stainless Steel · 1.4941 temper comparison
1.4941 1/4H and 1.4941-AW are two conditions of the same stainless steel grade, 1.4941: 1/4H (quarter hard) versus AW (as-welded deposit). The chemistry is identical, so every difference below comes from the condition. 1.4941 1/4H is the stronger of the two: yield strength 550 MPa (79.8 ksi) against 300 MPa (43.5 ksi) for 1.4941-AW, about 83% more; tensile strength follows at 780 MPa (113 ksi) vs 550 MPa (79.8 ksi). In exchange, 1.4941-AW is the more ductile: elongation 30% versus 18% for 1.4941 1/4H, and 1.4941 1/4H is harder (250 HB vs 175 HB). 1.4941-AW runs hotter in service (650°C vs 300°C continuous).
1.4941 1/4HChoose it when strength drives the design.
1.4941-AWChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4941 1/4H vs 1.4941-AW: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 166 GPa24.1 Msi · Poisson's Ratio 0.3 · Fracture Toughness (K_IC) 150 MPa·√m137 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 7.9 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,425°C2,597 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 15 W/m·K8.7 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.5 µm/m·K9.2 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 2.4 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 35 / 100 · Brazeability / Solderability 60 / 100 · Polishability 72 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 4.5 kg CO₂/kg · Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4941 1/4H vs 1.4941-AW — frequently asked
Is 1.4941 1/4H stronger than 1.4941-AW?
Yes. 1.4941 1/4H has a typical yield strength of 550 MPa (79.8 ksi) against 300 MPa (43.5 ksi) for 1.4941-AW — about 83% more. Tensile strength is 780 MPa (113 ksi) vs 550 MPa (79.8 ksi).
Which condition does FabDigit quote by default, 1/4H or AW?
AT is the default 1.4941 condition in the FabDigit quote flow (neither 1/4H nor AW). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4941 1/4H or 1.4941-AW?
1.4941 1/4H, by a small margin. Both rate fair for machinability — 40/100 against 35/100 for 1.4941-AW; for welding the order is 1.4941 1/4H first (very good, 75/100) then 1.4941-AW (very good, 70/100).