Stainless Steel 1.4938 +A vs 1.4938 +QT1100
Stainless Steel · 1.4938 temper comparison
1.4938 +A and 1.4938 +QT1100 are two conditions of the same stainless steel grade, 1.4938: +A (annealed) versus +QT1100 (quenched and tempered at lower temperature, 1000–1200 MPa). The chemistry is identical, so every difference below comes from the condition. 1.4938 +QT1100 is the stronger of the two: yield strength 930 MPa (135 ksi) against 520 MPa (75.4 ksi) for 1.4938 +A, about 79% more; tensile strength follows at 1,100 MPa (160 ksi) vs 790 MPa (115 ksi). In exchange, 1.4938 +A is the more ductile: elongation 20% versus 14% for 1.4938 +QT1100, and 1.4938 +QT1100 is harder (340 HB vs 240 HB). 1.4938 +QT1100 runs hotter in service (500°C vs 450°C continuous). On the shop floor, 1.4938 +A machines more easily (fair vs poor) and 1.4938 +A welds better (fair vs poor).
1.4938 +AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
1.4938 +QT1100Choose it when strength drives the design, or when the part sees heat.
1.4938 +A vs 1.4938 +QT1100: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 216 GPa31.3 Msi · Shear Modulus 83 GPa12 Msi · Bulk Modulus 166 GPa24.1 Msi · Poisson's Ratio 0.3 · Compressive Strength 820 MPa119 ksi · Shear Strength 590 MPa85.6 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.75 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 24 W/m·K13.9 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 40 / 100 · Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 4.3 kg CO₂/kg · Embodied Water 190 L/kg22.8 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4938 +A vs 1.4938 +QT1100 — frequently asked
Is 1.4938 +QT1100 stronger than 1.4938 +A?
Yes. 1.4938 +QT1100 has a typical yield strength of 930 MPa (135 ksi) against 520 MPa (75.4 ksi) for 1.4938 +A — about 79% more. Tensile strength is 1,100 MPa (160 ksi) vs 790 MPa (115 ksi).
Which condition does FabDigit quote by default, +A or +QT1100?
+QT is the default 1.4938 condition in the FabDigit quote flow (neither +A nor +QT1100). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4938 +A or 1.4938 +QT1100?
1.4938 +A. Its machinability rates fair (45/100) against poor (30/100) for 1.4938 +QT1100; for welding the order is 1.4938 +A first (fair, 40/100) then 1.4938 +QT1100 (poor, 30/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4938 +A and 1.4938 +QT1100 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.