Stainless Steel 1.4560 1/2H vs 1.4560-FH
Stainless Steel · 1.4560 temper comparison
1.4560 1/2H and 1.4560-FH are two conditions of the same stainless steel grade, 1.4560: 1/2H (half hard) versus FH (full hard). The chemistry is identical, so every difference below comes from the condition. 1.4560-FH is the stronger of the two: yield strength 1,050 MPa (152 ksi) against 700 MPa (102 ksi) for 1.4560 1/2H, about 50% more; tensile strength follows at 1,250 MPa (181 ksi) vs 900 MPa (131 ksi). In exchange, 1.4560 1/2H is the more ductile: elongation 15% versus 5% for 1.4560-FH, and 1.4560-FH is harder (370 HB vs 285 HB). On the shop floor, 1.4560 1/2H machines more easily (52 vs 42 out of 100) and 1.4560 1/2H welds better (good vs fair).
1.4560 1/2HChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
1.4560-FHChoose it when strength drives the design.
1.4560 1/2H vs 1.4560-FH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 193 GPa28 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.29 · Hardness, Rockwell B 80 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.9 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 15 W/m·K8.7 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.5 µm/m·K9.2 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.4 % IACS · Electrical Resistivity 7.3×10⁻⁷ Ω·m28.7 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 53 MJ/kg22,786 BTU/lb · Embodied Carbon (primary production) 5 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4560 1/2H vs 1.4560-FH — frequently asked
Is 1.4560-FH stronger than 1.4560 1/2H?
Yes. 1.4560-FH has a typical yield strength of 1,050 MPa (152 ksi) against 700 MPa (102 ksi) for 1.4560 1/2H — about 50% more. Tensile strength is 1,250 MPa (181 ksi) vs 900 MPa (131 ksi).
Which condition does FabDigit quote by default, 1/2H or FH?
A is the default 1.4560 condition in the FabDigit quote flow (neither 1/2H nor FH). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4560 1/2H or 1.4560-FH?
1.4560 1/2H, by a small margin. Both rate fair for machinability — 52/100 against 42/100 for 1.4560-FH; for welding the order is 1.4560 1/2H first (good, 60/100) then 1.4560-FH (fair, 45/100).