Stainless Steel 1.4558-ANN vs 1.4558-CD
Stainless Steel · 1.4558 temper comparison
1.4558-ANN and 1.4558-CD are two conditions of the same stainless steel grade, 1.4558: ANN (annealed) versus CD (cold drawn). The chemistry is identical, so every difference below comes from the condition. 1.4558-CD is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 240 MPa (34.8 ksi) for 1.4558-ANN, about 100% more; tensile strength follows at 690 MPa (100 ksi) vs 550 MPa (79.8 ksi). In exchange, 1.4558-ANN is the more ductile: elongation 42% versus 22% for 1.4558-CD, and 1.4558-CD is harder (200 HB vs 140 HB). 1.4558-ANN runs hotter in service (800°C vs 500°C continuous).
1.4558-ANNChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4558-CDChoose it when strength drives the design.
1.4558-ANN vs 1.4558-CD: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 196 GPa28.4 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 200 GPa29 Msi · Poisson's Ratio 0.34 · Shear Strength 380 MPa55.1 ksi · Charpy V-Notch Impact (RT) 150 J111 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 7.94 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,357°C2,475 °F · Liquidus Temperature 1,385°C2,525 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 11.5 W/m·K6.6 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 14.4 µm/m·K8 µin/in·°F · Latent Heat of Fusion 285 J/g123 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.7 % IACS · Electrical Resistivity 9.9×10⁻⁷ Ω·m39 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 70 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 25% · Weldability 80 / 100 · Brazeability / Solderability 60 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 90 MJ/kg38,693 BTU/lb · Embodied Carbon (primary production) 7 kg CO₂/kg · Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4558-ANN vs 1.4558-CD — frequently asked
Is 1.4558-CD stronger than 1.4558-ANN?
Yes. 1.4558-CD has a typical yield strength of 480 MPa (69.6 ksi) against 240 MPa (34.8 ksi) for 1.4558-ANN — about 100% more. Tensile strength is 690 MPa (100 ksi) vs 550 MPa (79.8 ksi).
Which condition does FabDigit quote by default, ANN or CD?
ANN is the default 1.4558 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4558-ANN or 1.4558-CD?
1.4558-CD. Its machinability rates fair (35/100) against poor (30/100) for 1.4558-ANN.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4558-ANN and 1.4558-CD side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.