Stainless Steel 1.4423 +A vs 1.4423 +QT800
Stainless Steel · 1.4423 temper comparison
1.4423 +A and 1.4423 +QT800 are two conditions of the same stainless steel grade, 1.4423: +A (annealed) versus +QT800 (quenched and tempered to Rm 800–950 MPa). The chemistry is identical, so every difference below comes from the condition. 1.4423 +QT800 is the stronger of the two: yield strength 680 MPa (98.6 ksi) against 600 MPa (87 ksi) for 1.4423 +A, about 13% more; tensile strength follows at 870 MPa (126 ksi) vs 800 MPa (116 ksi). In exchange, 1.4423 +A is the more ductile: elongation 20% versus 18% for 1.4423 +QT800, and 1.4423 +QT800 is harder (27 HRC vs 25 HRC).
1.4423 +AChoose it when the part is bent, formed or impact-loaded.
1.4423 +QT800Choose it when strength drives the design.
1.4423 +A vs 1.4423 +QT800: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Fracture Toughness (K_IC) 150 MPa·√m137 ksi·√in · Charpy V-Notch Impact (RT) 100 J73.8 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,465°C2,669 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 16 W/m·K9.2 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 300°C572 °F · Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.3 % IACS · Electrical Resistivity 7.5×10⁻⁷ Ω·m29.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 60 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 50 / 100 · Brazeability / Solderability 45 / 100 · Polishability 78 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 4.5 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4423 +A vs 1.4423 +QT800 — frequently asked
Is 1.4423 +QT800 stronger than 1.4423 +A?
Yes. 1.4423 +QT800 has a typical yield strength of 680 MPa (98.6 ksi) against 600 MPa (87 ksi) for 1.4423 +A — about 13% more. Tensile strength is 870 MPa (126 ksi) vs 800 MPa (116 ksi).
Which condition does FabDigit quote by default, +A or +QT800?
+QT900 is the default 1.4423 condition in the FabDigit quote flow (neither +A nor +QT800). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4423 +A or 1.4423 +QT800?
1.4423 +A, by a small margin. Both rate fair for machinability — 45/100 against 40/100 for 1.4423 +QT800.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4423 +A and 1.4423 +QT800 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.