Stainless Steel 1.4122 +A vs 1.4122 +QT800
Stainless Steel · 1.4122 temper comparison
1.4122 +A and 1.4122 +QT800 are two conditions of the same stainless steel grade, 1.4122: +A (annealed) versus +QT800 (quenched and tempered, Rm 800–1000 MPa). The chemistry is identical, so every difference below comes from the condition. 1.4122 +QT800 is the stronger of the two: yield strength 680 MPa (98.6 ksi) against 460 MPa (66.7 ksi) for 1.4122 +A, about 48% more; tensile strength follows at 900 MPa (131 ksi) vs 780 MPa (113 ksi). In exchange, 1.4122 +A is the more ductile: elongation 18% versus 12% for 1.4122 +QT800, and 1.4122 +QT800 is harder (285 HB vs 240 HB). On the shop floor, 1.4122 +A machines more easily (fair vs poor).
1.4122 +AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
1.4122 +QT800Choose it when strength drives the design.
1.4122 +A vs 1.4122 +QT800: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 216 GPa31.3 Msi · Shear Modulus 83 GPa12 Msi · Bulk Modulus 163 GPa23.6 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 45 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 4.8 kg CO₂/kg · Embodied Water 110 L/kg13.2 gal/lb · Typical Recycled Content 50%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4122 +A vs 1.4122 +QT800 — frequently asked
Is 1.4122 +QT800 stronger than 1.4122 +A?
Yes. 1.4122 +QT800 has a typical yield strength of 680 MPa (98.6 ksi) against 460 MPa (66.7 ksi) for 1.4122 +A — about 48% more. Tensile strength is 900 MPa (131 ksi) vs 780 MPa (113 ksi).
Which condition does FabDigit quote by default, +A or +QT800?
+A is the default 1.4122 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4122 +A or 1.4122 +QT800?
1.4122 +A. Its machinability rates fair (45/100) against poor (30/100) for 1.4122 +QT800; for welding the order is 1.4122 +A first (poor, 22/100) then 1.4122 +QT800 (poor, 15/100).