Solder & Low-Melting Alloy B23 Grade 10 vs Corroding Lead
Solder & Low-Melting Alloy · grade comparison
Solder & Low-Melting Alloy B23 Grade 10 and Corroding Lead are both solder & low-melting alloy grades. B23 Grade 10 is the stronger of the two: yield strength 26 MPa (3.77 ksi) against 6 MPa (0.87 ksi) for Corroding Lead, about 4.3 times as much; tensile strength follows at 60 MPa (8.7 ksi) vs 13 MPa (1.89 ksi). In exchange, Corroding Lead is the more ductile: elongation 35% versus 3% for B23 Grade 10, and B23 Grade 10 is harder (21 HB vs 5 HB). B23 Grade 10 is lighter (10 g/cm³ vs 11.34 g/cm³ for Corroding Lead) and B23 Grade 10 is stiffer (28 GPa vs 14 GPa). On the shop floor, B23 Grade 10 machines more easily (excellent vs good), Corroding Lead welds better (good vs poor), and Corroding Lead sits in a lower cost tier (standard, $$) than B23 Grade 10 (premium, $$$).
B23 Grade 10Choose it when strength drives the design, or when weight is the constraint.
Corroding LeadChoose it when the part is bent, formed or impact-loaded, or when it will be welded.
B23 Grade 10 vs Corroding Lead: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all solder & low-melting alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all solder & low-melting alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.55 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Castability 90 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Carbon (primary production) 1.8 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every solder & low-melting alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | B23 Grade 10 | Corroding Lead |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
B23 Grade 10 vs Corroding Lead — frequently asked
Is B23 Grade 10 stronger than Corroding Lead?
Yes. B23 Grade 10 has a typical yield strength of 26 MPa (3.77 ksi) against 6 MPa (0.87 ksi) for Corroding Lead — about 4.3 times as much. Tensile strength is 60 MPa (8.7 ksi) vs 13 MPa (1.89 ksi).
Which is cheaper, B23 Grade 10 or Corroding Lead?
Corroding Lead is the lower-cost material: it sits in the standard tier ($$) while B23 Grade 10 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, B23 Grade 10 or Corroding Lead?
B23 Grade 10. Its machinability rates excellent (90/100) against good (55/100) for Corroding Lead; for welding the order is Corroding Lead first (good, 60/100) then B23 Grade 10 (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in B23 Grade 10 and Corroding Lead side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.