Refractory Metal Zr 702C-A vs Zr 702C-HIP
Refractory Metal · Zr 702C temper comparison
Zr 702C-A and Zr 702C-HIP are two conditions of the same refractory metal grade, Zr 702C: A (solution annealed) versus HIP (hot isostatic pressed). The chemistry is identical, so every difference below comes from the condition. Zr 702C-HIP is the stronger of the two: yield strength 255 MPa (37 ksi) against 230 MPa (33.4 ksi) for Zr 702C-A, about 11% more; tensile strength follows at 460 MPa (66.7 ksi) vs 420 MPa (60.9 ksi). Zr 702C-HIP is harder — 148 HB against 140 HB for Zr 702C-A — which matters for wear surfaces and threads.
Zr 702C-HIPChoose it when strength drives the design, or when surface hardness matters.
Zr 702C-A vs Zr 702C-HIP: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all refractory metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all refractory metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Shear Modulus 36 GPa5.2 Msi · Bulk Modulus 90 GPa13.1 Msi · Poisson's Ratio 0.34 · Elongation at Break 20%
Physical
Density and transition temperatures.
Same in both: Density 6.51 g/cm³0.24 lb/in³ · Melting Point (Solidus) 1,852°C3,366 °F · Liquidus Temperature 1,855°C3,371 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 22 W/m·K12.7 BTU/hr·ft·°F · Specific Heat Capacity 285 J/kg·K0.07 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 5.9 µm/m·K3.3 µin/in·°F · Latent Heat of Fusion 155 J/g66.6 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 55 / 100 · Brazeability / Solderability 25 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 1,250 MJ/kg537,404 BTU/lb · Embodied Carbon (primary production) 80 kg CO₂/kg · Embodied Water 600 L/kg71.9 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every refractory metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Zr 702C-A vs Zr 702C-HIP — frequently asked
Is Zr 702C-HIP stronger than Zr 702C-A?
Yes. Zr 702C-HIP has a typical yield strength of 255 MPa (37 ksi) against 230 MPa (33.4 ksi) for Zr 702C-A — about 11% more. Tensile strength is 460 MPa (66.7 ksi) vs 420 MPa (60.9 ksi).
Which condition does FabDigit quote by default, A or HIP?
F is the default Zr 702C condition in the FabDigit quote flow (neither A nor HIP). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose Zr 702C-A over Zr 702C-HIP?
Pick Zr 702C-HIP when strength drives the design, or when surface hardness matters.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Zr 702C-A and Zr 702C-HIP side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.