Precious Metal PtRu10 Annealed vs PtRu10 Spring
Precious Metal · PtRu10 temper comparison
PtRu10 Annealed and PtRu10 Spring are two conditions of the same precious metal grade, PtRu10: Annealed versus Spring (spring hard). The chemistry is identical, so every difference below comes from the condition. PtRu10 Spring is the stronger of the two: yield strength 950 MPa (138 ksi) against 250 MPa (36.3 ksi) for PtRu10 Annealed, about 3.8 times as much; tensile strength follows at 1,050 MPa (152 ksi) vs 520 MPa (75.4 ksi). In exchange, PtRu10 Annealed is the more ductile: elongation 28% versus 2% for PtRu10 Spring, and PtRu10 Spring is harder (270 HB vs 133 HB). PtRu10 Annealed runs hotter in service (500°C vs 200°C continuous). On the shop floor, PtRu10 Spring machines more easily (fair vs poor) and PtRu10 Annealed welds better (very good vs fair).
PtRu10 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
PtRu10 SpringChoose it when strength drives the design, or when the part is machined in volume.
PtRu10 Annealed vs PtRu10 Spring: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 75 GPa10.9 Msi · Bulk Modulus 255 GPa37 Msi · Poisson's Ratio 0.38 · Hardness, Rockwell B 76 HRB
Physical
Density and transition temperatures.
Same in both: Density 20 g/cm³0.72 lb/in³ · Melting Point (Solidus) 1,780°C3,236 °F · Liquidus Temperature 1,800°C3,272 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 135 J/kg·K0.03 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 9 µm/m·K5 µin/in·°F · Latent Heat of Fusion 120 J/g51.6 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0.25 V · Corrosion Resistance 96 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 40 / 100 · Brazeability / Solderability 80 / 100 · Polishability 90 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 220,000 MJ/kg9.46×10⁷ BTU/lb · Embodied Carbon (primary production) 13,500 kg CO₂/kg · Embodied Water 200,000 L/kg23,965 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PtRu10 Annealed vs PtRu10 Spring — frequently asked
Is PtRu10 Spring stronger than PtRu10 Annealed?
Yes. PtRu10 Spring has a typical yield strength of 950 MPa (138 ksi) against 250 MPa (36.3 ksi) for PtRu10 Annealed — about 3.8 times as much. Tensile strength is 1,050 MPa (152 ksi) vs 520 MPa (75.4 ksi).
Which condition does FabDigit quote by default, Annealed or Spring?
Annealed is the default PtRu10 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, PtRu10 Annealed or PtRu10 Spring?
PtRu10 Spring. Its machinability rates fair (42/100) against poor (30/100) for PtRu10 Annealed; for welding the order is PtRu10 Annealed first (very good, 70/100) then PtRu10 Spring (fair, 50/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in PtRu10 Annealed and PtRu10 Spring side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.