Pd99.9 AS-CAST and Pd99.9-H01 are two conditions of the same precious metal grade, Pd99.9: AS-CAST versus H01 (quarter hard). The chemistry is identical, so every difference below comes from the condition. Pd99.9-H01 is the stronger of the two: yield strength 170 MPa (24.7 ksi) against 50 MPa (7.25 ksi) for Pd99.9 AS-CAST, about 3.4 times as much; tensile strength follows at 230 MPa (33.4 ksi) vs 165 MPa (23.9 ksi). In exchange, Pd99.9 AS-CAST is the more ductile: elongation 25% versus 16% for Pd99.9-H01, and Pd99.9-H01 is harder (64 HB vs 38 HB). Pd99.9 AS-CAST runs hotter in service (500°C vs 300°C continuous).
Pd99.9 AS-CASTChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Pd99.9-H01Choose it when strength drives the design.
Pd99.9 AS-CAST vs Pd99.9-H01: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 180 GPa26.1 Msi · Poisson's Ratio 0.39
Physical
Density and transition temperatures.
Same in both: Density 12.02 g/cm³0.43 lb/in³ · Melting Point (Solidus) 1,555°C2,831 °F · Liquidus Temperature 1,555°C2,831 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 244 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.8 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 157 J/g67.5 BTU/lb · Min Service Temperature -253°C-423 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0.25 V · Corrosion Resistance 92 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 65 / 100 · Brazeability / Solderability 85 / 100 · Polishability 90 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 60,000 MJ/kg2.58×10⁷ BTU/lb · Embodied Carbon (primary production) 3,900 kg CO₂/kg · Embodied Water 250,000 L/kg29,957 gal/lb · Typical Recycled Content 28%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Pd99.9 AS-CAST vs Pd99.9-H01 — frequently asked
Is Pd99.9-H01 stronger than Pd99.9 AS-CAST?
Yes. Pd99.9-H01 has a typical yield strength of 170 MPa (24.7 ksi) against 50 MPa (7.25 ksi) for Pd99.9 AS-CAST — about 3.4 times as much. Tensile strength is 230 MPa (33.4 ksi) vs 165 MPa (23.9 ksi).
Which condition does FabDigit quote by default, AS-CAST or H01?
Annealed is the default Pd99.9 condition in the FabDigit quote flow (neither AS-CAST nor H01). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, Pd99.9 AS-CAST or Pd99.9-H01?
Pd99.9-H01. Its machinability rates fair (35/100) against poor (30/100) for Pd99.9 AS-CAST; for welding the order is Pd99.9 AS-CAST first (very good, 80/100) then Pd99.9-H01 (very good, 75/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Pd99.9 AS-CAST and Pd99.9-H01 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.