Precious Metal BAg-1 vs BAg-8
Precious Metal · grade comparison
Precious Metal BAg-1 and BAg-8 are both precious metal grades. BAg-1 is the stronger of the two: yield strength 200 MPa (29 ksi) against 160 MPa (23.2 ksi) for BAg-8, about 25% more; tensile strength follows at 414 MPa (60 ksi) vs 380 MPa (55.1 ksi). BAg-1 is harder — 90 HB against 65 HB for BAg-8 — which matters for wear surfaces and threads. BAg-1 is lighter (9.3 g/cm³ vs 10 g/cm³ for BAg-8) and BAg-8 is stiffer (90 GPa vs 83 GPa). On the shop floor, BAg-8 machines more easily (good vs fair), BAg-8 welds better (30 vs 15 out of 100), and BAg-8 forms better (excellent vs very good).
BAg-1Choose it when strength drives the design, or when surface hardness matters.
BAg-8Choose it when the part sees heat, or when the part is machined in volume.
BAg-1 vs BAg-8: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Bulk Modulus
Reduction in Area
Fatigue Strength (Endurance Limit)
Same in both: Poisson's Ratio 0.36
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Castability
Polishability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Brazeability / Solderability 98 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | BAg-1 | BAg-8 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
BAg-1 vs BAg-8 — frequently asked
Is BAg-1 stronger than BAg-8?
Yes. BAg-1 has a typical yield strength of 200 MPa (29 ksi) against 160 MPa (23.2 ksi) for BAg-8 — about 25% more. Tensile strength is 414 MPa (60 ksi) vs 380 MPa (55.1 ksi).
Which is cheaper, BAg-1 or BAg-8?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, BAg-1 or BAg-8?
BAg-8. Its machinability rates good (55/100) against fair (40/100) for BAg-1; for welding the order is BAg-8 first (poor, 30/100) then BAg-1 (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in BAg-1 and BAg-8 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.