Precious Metal B522 Class II 1/2H vs B522 Class II-H
Precious Metal · B522 Class II temper comparison
B522 Class II 1/2H and B522 Class II-H are two conditions of the same precious metal grade, B522 Class II: 1/2H (half hard) versus H (hardened). The chemistry is identical, so every difference below comes from the condition. B522 Class II-H is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 420 MPa (60.9 ksi) for B522 Class II 1/2H, about 48% more; tensile strength follows at 720 MPa (104 ksi) vs 560 MPa (81.2 ksi). In exchange, B522 Class II 1/2H is the more ductile: elongation 10% versus 3% for B522 Class II-H, and B522 Class II-H is harder (200 HB vs 90 HB). B522 Class II 1/2H runs hotter in service (250°C vs 200°C continuous).
B522 Class II 1/2HChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
B522 Class II-HChoose it when strength drives the design.
B522 Class II 1/2H vs B522 Class II-H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
B522 Class II 1/2HB522 Class II-H
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 32 GPa4.6 Msi · Bulk Modulus 145 GPa21 Msi · Poisson's Ratio 0.4
Physical
Density and transition temperatures.
Same in both: Density 16 g/cm³0.58 lb/in³ · Melting Point (Solidus) 1,035°C1,895 °F · Liquidus Temperature 1,065°C1,949 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 150 J/kg·K0.04 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 15 µm/m·K8.3 µin/in·°F · Latent Heat of Fusion 75 J/g32.2 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0.25 V · Corrosion Resistance 97 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 35% · Castability 70 / 100 · Brazeability / Solderability 90 / 100 · Polishability 92 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 180,000 MJ/kg7.74×10⁷ BTU/lb · Embodied Carbon (primary production) 12,000 kg CO₂/kg · Embodied Water 150,000 L/kg17,974 gal/lb · Typical Recycled Content 85%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
B522 Class II 1/2H vs B522 Class II-H — frequently asked
Is B522 Class II-H stronger than B522 Class II 1/2H?
Yes. B522 Class II-H has a typical yield strength of 620 MPa (89.9 ksi) against 420 MPa (60.9 ksi) for B522 Class II 1/2H — about 48% more. Tensile strength is 720 MPa (104 ksi) vs 560 MPa (81.2 ksi).
Which condition does FabDigit quote by default, 1/2H or H?
ANN is the default B522 Class II condition in the FabDigit quote flow (neither 1/2H nor H). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, B522 Class II 1/2H or B522 Class II-H?
B522 Class II-H. Its machinability rates good (55/100) against fair (50/100) for B522 Class II 1/2H; for welding the order is B522 Class II 1/2H first (good, 60/100) then B522 Class II-H (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in B522 Class II 1/2H and B522 Class II-H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.