Precious Metal AgCu10 Annealed vs AgCu10-H01
Precious Metal · AgCu10 temper comparison
AgCu10 Annealed and AgCu10-H01 are two conditions of the same precious metal grade, AgCu10: Annealed versus H01 (quarter hard). The chemistry is identical, so every difference below comes from the condition. AgCu10-H01 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 115 MPa (16.7 ksi) for AgCu10 Annealed, about 117% more; tensile strength follows at 350 MPa (50.8 ksi) vs 285 MPa (41.3 ksi). In exchange, AgCu10 Annealed is the more ductile: elongation 35% versus 18% for AgCu10-H01, and AgCu10-H01 is harder (82 HB vs 60 HB). AgCu10 Annealed runs hotter in service (250°C vs 200°C continuous).
AgCu10 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
AgCu10-H01Choose it when strength drives the design.
AgCu10 Annealed vs AgCu10-H01: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 78 GPa11.3 Msi · Shear Modulus 29 GPa4.2 Msi · Bulk Modulus 103 GPa14.9 Msi · Poisson's Ratio 0.37
Physical
Density and transition temperatures.
Same in both: Density 10.31 g/cm³0.37 lb/in³ · Melting Point (Solidus) 779°C1,434 °F · Liquidus Temperature 875°C1,607 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 237 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 19 µm/m·K10.6 µin/in·°F · Latent Heat of Fusion 105 J/g45.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0.12 V · Corrosion Resistance 78 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Castability 75 / 100 · Brazeability / Solderability 95 / 100 · Polishability 95 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 1,400 MJ/kg601,892 BTU/lb · Embodied Carbon (primary production) 95 kg CO₂/kg · Embodied Water 22,000 L/kg2,636 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
AgCu10 Annealed vs AgCu10-H01 — frequently asked
Is AgCu10-H01 stronger than AgCu10 Annealed?
Yes. AgCu10-H01 has a typical yield strength of 250 MPa (36.3 ksi) against 115 MPa (16.7 ksi) for AgCu10 Annealed — about 117% more. Tensile strength is 350 MPa (50.8 ksi) vs 285 MPa (41.3 ksi).
Which condition does FabDigit quote by default, Annealed or H01?
Annealed is the default AgCu10 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, AgCu10 Annealed or AgCu10-H01?
AgCu10-H01, by a small margin. Both rate good for machinability — 60/100 against 55/100 for AgCu10 Annealed.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AgCu10 Annealed and AgCu10-H01 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.