Precious Metal 88Ag-12SnO2 Annealed vs 88Ag-12SnO2-H
Precious Metal · 88Ag-12SnO2 temper comparison
88Ag-12SnO2 Annealed and 88Ag-12SnO2-H are two conditions of the same precious metal grade, 88Ag-12SnO2: Annealed versus H (hardened). The chemistry is identical, so every difference below comes from the condition. 88Ag-12SnO2-H is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 150 MPa (21.8 ksi) for 88Ag-12SnO2 Annealed, about 67% more; tensile strength follows at 300 MPa (43.5 ksi) vs 235 MPa (34.1 ksi). In exchange, 88Ag-12SnO2 Annealed is the more ductile: elongation 20% versus 8% for 88Ag-12SnO2-H, and 88Ag-12SnO2-H is harder (95 HB vs 67 HB). 88Ag-12SnO2 Annealed runs hotter in service (300°C vs 250°C continuous).
88Ag-12SnO2 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
88Ag-12SnO2-HChoose it when strength drives the design.
88Ag-12SnO2 Annealed vs 88Ag-12SnO2-H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
88Ag-12SnO2 Annealed88Ag-12SnO2-H
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 32 GPa4.6 Msi · Bulk Modulus 105 GPa15.2 Msi · Poisson's Ratio 0.36
Physical
Density and transition temperatures.
Same in both: Density 9.9 g/cm³0.36 lb/in³ · Melting Point (Solidus) 961°C1,762 °F · Liquidus Temperature 962°C1,764 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 240 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18 µm/m·K10 µin/in·°F · Latent Heat of Fusion 92 J/g39.6 BTU/lb · Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0.05 V · Corrosion Resistance 80 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 25 / 100 · Brazeability / Solderability 85 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 1,300 MJ/kg558,900 BTU/lb · Embodied Carbon (primary production) 100 kg CO₂/kg · Embodied Water 400 L/kg47.9 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
88Ag-12SnO2 Annealed vs 88Ag-12SnO2-H — frequently asked
Is 88Ag-12SnO2-H stronger than 88Ag-12SnO2 Annealed?
Yes. 88Ag-12SnO2-H has a typical yield strength of 250 MPa (36.3 ksi) against 150 MPa (21.8 ksi) for 88Ag-12SnO2 Annealed — about 67% more. Tensile strength is 300 MPa (43.5 ksi) vs 235 MPa (34.1 ksi).
Which condition does FabDigit quote by default, Annealed or H?
H is the default 88Ag-12SnO2 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 88Ag-12SnO2 Annealed or 88Ag-12SnO2-H?
88Ag-12SnO2-H, by a small margin. Both rate fair for machinability — 40/100 against 35/100 for 88Ag-12SnO2 Annealed; for welding the order is 88Ag-12SnO2 Annealed first (good, 60/100) then 88Ag-12SnO2-H (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 88Ag-12SnO2 Annealed and 88Ag-12SnO2-H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.