Precious Metal 85Ag-15Ni-H08 vs 85Ag-15Ni-O
Precious Metal · 85Ag-15Ni temper comparison
85Ag-15Ni-H08 and 85Ag-15Ni-O are two conditions of the same precious metal grade, 85Ag-15Ni: H08 (spring hard) versus O (annealed). The chemistry is identical, so every difference below comes from the condition. 85Ag-15Ni-H08 is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 95 MPa (13.8 ksi) for 85Ag-15Ni-O, about 4.0 times as much; tensile strength follows at 420 MPa (60.9 ksi) vs 230 MPa (33.4 ksi). In exchange, 85Ag-15Ni-O is the more ductile: elongation 25% versus 2% for 85Ag-15Ni-H08, and 85Ag-15Ni-H08 is harder (115 HB vs 57 HB). 85Ag-15Ni-O is stiffer (100 GPa vs 95 GPa) and 85Ag-15Ni-O runs hotter in service (300°C vs 150°C continuous). On the shop floor, 85Ag-15Ni-H08 machines more easily (45 vs 35 out of 100).
85Ag-15Ni-H08Choose it when strength drives the design, or when the part is machined in volume.
85Ag-15Ni-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
85Ag-15Ni-H08 vs 85Ag-15Ni-O: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Bulk Modulus 118 GPa17.1 Msi · Poisson's Ratio 0.36
Physical
Density and transition temperatures.
Density
Liquidus Temperature
Same in both: Melting Point (Solidus) 961°C1,762 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Thermal Expansion (CTE, 20–100 °C) 18.5 µm/m·K10.3 µin/in·°F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) 0 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 30% · Weldability 55 / 100 · Castability 10 / 100
Sustainability
Primary-production footprint per kilogram.
Typical Recycled Content
Same in both: Embodied Energy (primary production) 1,300 MJ/kg558,900 BTU/lb · Embodied Carbon (primary production) 110 kg CO₂/kg · Embodied Water 2,500 L/kg300 gal/lb
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
85Ag-15Ni-H08 vs 85Ag-15Ni-O — frequently asked
Is 85Ag-15Ni-H08 stronger than 85Ag-15Ni-O?
Yes. 85Ag-15Ni-H08 has a typical yield strength of 380 MPa (55.1 ksi) against 95 MPa (13.8 ksi) for 85Ag-15Ni-O — about 4.0 times as much. Tensile strength is 420 MPa (60.9 ksi) vs 230 MPa (33.4 ksi).
Which condition does FabDigit quote by default, H08 or O?
O is the default 85Ag-15Ni condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 85Ag-15Ni-H08 or 85Ag-15Ni-O?
85Ag-15Ni-H08, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for 85Ag-15Ni-O.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 85Ag-15Ni-H08 and 85Ag-15Ni-O side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.