Precious Metal 833 Silver-H02 vs 833 Silver-H08
Precious Metal · 833 Silver temper comparison
833 Silver-H02 and 833 Silver-H08 are two conditions of the same precious metal grade, 833 Silver: H02 (half hard) versus H08 (spring hard). The chemistry is identical, so every difference below comes from the condition. 833 Silver-H08 is the stronger of the two: yield strength 500 MPa (72.5 ksi) against 330 MPa (47.9 ksi) for 833 Silver-H02, about 52% more; tensile strength follows at 560 MPa (81.2 ksi) vs 420 MPa (60.9 ksi). In exchange, 833 Silver-H02 is the more ductile: elongation 12% versus 3% for 833 Silver-H08, and 833 Silver-H08 is harder (142 HB vs 104 HB). 833 Silver-H02 runs hotter in service (150°C vs 130°C continuous). On the shop floor, 833 Silver-H02 welds better (50 vs 40 out of 100).
833 Silver-H02Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
833 Silver-H08Choose it when strength drives the design.
833 Silver-H02 vs 833 Silver-H08: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 29 GPa4.2 Msi · Bulk Modulus 103 GPa14.9 Msi · Poisson's Ratio 0.37
Physical
Density and transition temperatures.
Same in both: Density 10.2 g/cm³0.37 lb/in³ · Melting Point (Solidus) 779°C1,434 °F · Liquidus Temperature 830°C1,526 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 255 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.7 µm/m·K10.4 µin/in·°F · Latent Heat of Fusion 110 J/g47.3 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 60 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 80 / 100 · Brazeability / Solderability 95 / 100 · Polishability 95 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 1,250 MJ/kg537,404 BTU/lb · Embodied Carbon (primary production) 85 kg CO₂/kg · Embodied Water 2,500 L/kg300 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
833 Silver-H02 vs 833 Silver-H08 — frequently asked
Is 833 Silver-H08 stronger than 833 Silver-H02?
Yes. 833 Silver-H08 has a typical yield strength of 500 MPa (72.5 ksi) against 330 MPa (47.9 ksi) for 833 Silver-H02 — about 52% more. Tensile strength is 560 MPa (81.2 ksi) vs 420 MPa (60.9 ksi).
Which condition does FabDigit quote by default, H02 or H08?
O is the default 833 Silver condition in the FabDigit quote flow (neither H02 nor H08). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 833 Silver-H02 or 833 Silver-H08?
833 Silver-H08, by a small margin. Both rate good for machinability — 68/100 against 62/100 for 833 Silver-H02; for welding the order is 833 Silver-H02 first (fair, 50/100) then 833 Silver-H08 (fair, 40/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 833 Silver-H02 and 833 Silver-H08 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.