833 Silver-F and 833 Silver-H01 are two conditions of the same precious metal grade, 833 Silver: F (as fabricated) versus H01 (quarter hard). The chemistry is identical, so every difference below comes from the condition. 833 Silver-H01 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 115 MPa (16.7 ksi) for 833 Silver-F, about 117% more; tensile strength follows at 360 MPa (52.2 ksi) vs 280 MPa (40.6 ksi). 833 Silver-H01 is the more ductile: elongation 20% versus 15% for 833 Silver-F, and 833 Silver-H01 is harder (85 HB vs 64 HB). 833 Silver-F runs hotter in service (200°C vs 170°C continuous).
833 Silver-FChoose it when the part sees heat.
833 Silver-H01Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
833 Silver-F vs 833 Silver-H01: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 29 GPa4.2 Msi · Bulk Modulus 103 GPa14.9 Msi · Poisson's Ratio 0.37
Physical
Density and transition temperatures.
Same in both: Density 10.2 g/cm³0.37 lb/in³ · Melting Point (Solidus) 779°C1,434 °F · Liquidus Temperature 830°C1,526 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 340 W/m·K196 BTU/hr·ft·°F · Specific Heat Capacity 255 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.7 µm/m·K10.4 µin/in·°F · Latent Heat of Fusion 110 J/g47.3 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 80 / 100 · Brazeability / Solderability 95 / 100 · Polishability 95 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 1,250 MJ/kg537,404 BTU/lb · Embodied Carbon (primary production) 85 kg CO₂/kg · Embodied Water 2,500 L/kg300 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
833 Silver-F vs 833 Silver-H01 — frequently asked
Is 833 Silver-H01 stronger than 833 Silver-F?
Yes. 833 Silver-H01 has a typical yield strength of 250 MPa (36.3 ksi) against 115 MPa (16.7 ksi) for 833 Silver-F — about 117% more. Tensile strength is 360 MPa (52.2 ksi) vs 280 MPa (40.6 ksi).
Which condition does FabDigit quote by default, F or H01?
O is the default 833 Silver condition in the FabDigit quote flow (neither F nor H01). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, 833 Silver-F or 833 Silver-H01?
833 Silver-F. Its weldability rates good (60/100) against good (55/100) for 833 Silver-H01.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 833 Silver-F and 833 Silver-H01 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.