Precious Metal 60Pd-40Ag Annealed vs 60Pd-40Ag-FH
Precious Metal · 60Pd-40Ag temper comparison
60Pd-40Ag Annealed and 60Pd-40Ag-FH are two conditions of the same precious metal grade, 60Pd-40Ag: Annealed versus FH (full hard). The chemistry is identical, so every difference below comes from the condition. 60Pd-40Ag-FH is the stronger of the two: yield strength 700 MPa (102 ksi) against 180 MPa (26.1 ksi) for 60Pd-40Ag Annealed, about 3.9 times as much; tensile strength follows at 750 MPa (109 ksi) vs 400 MPa (58 ksi). In exchange, 60Pd-40Ag Annealed is the more ductile: elongation 30% versus 2.5% for 60Pd-40Ag-FH, and 60Pd-40Ag-FH is harder (180 HV vs 85 HV). 60Pd-40Ag Annealed runs hotter in service (500°C vs 280°C continuous). On the shop floor, 60Pd-40Ag-FH machines more easily (fair vs poor) and 60Pd-40Ag Annealed welds better (very good vs good).
60Pd-40Ag AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
60Pd-40Ag-FHChoose it when strength drives the design, or when the part is machined in volume.
60Pd-40Ag Annealed vs 60Pd-40Ag-FH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
60Pd-40Ag Annealed60Pd-40Ag-FH
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 115 GPa16.7 Msi · Shear Modulus 43 GPa6.2 Msi · Bulk Modulus 150 GPa21.8 Msi · Poisson's Ratio 0.37 · Reduction in Area 65% · Hardness, Brinell 82 HB
Physical
Density and transition temperatures.
Same in both: Density 11.36 g/cm³0.41 lb/in³ · Melting Point (Solidus) 1,290°C2,354 °F · Liquidus Temperature 1,330°C2,426 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 22 W/m·K12.7 BTU/hr·ft·°F · Specific Heat Capacity 240 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 14.5 µm/m·K8.1 µin/in·°F · Latent Heat of Fusion 135 J/g58 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0.2 V · Corrosion Resistance 92 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 30% · Castability 70 / 100 · Brazeability / Solderability 85 / 100 · Polishability 90 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 44,000 MJ/kg1.89×10⁷ BTU/lb · Embodied Carbon (primary production) 2,400 kg CO₂/kg · Embodied Water 180,000 L/kg21,569 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
60Pd-40Ag Annealed vs 60Pd-40Ag-FH — frequently asked
Is 60Pd-40Ag-FH stronger than 60Pd-40Ag Annealed?
Yes. 60Pd-40Ag-FH has a typical yield strength of 700 MPa (102 ksi) against 180 MPa (26.1 ksi) for 60Pd-40Ag Annealed — about 3.9 times as much. Tensile strength is 750 MPa (109 ksi) vs 400 MPa (58 ksi).
Which condition does FabDigit quote by default, Annealed or FH?
Annealed is the default 60Pd-40Ag condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 60Pd-40Ag Annealed or 60Pd-40Ag-FH?
60Pd-40Ag-FH. Its machinability rates fair (50/100) against poor (32/100) for 60Pd-40Ag Annealed; for welding the order is 60Pd-40Ag Annealed first (very good, 78/100) then 60Pd-40Ag-FH (good, 65/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 60Pd-40Ag Annealed and 60Pd-40Ag-FH side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.