Sumikasuper GF15 vs Sumikasuper GF30
Polymer · Sumikasuper grade comparison
Sumikasuper GF15 and Sumikasuper GF30 are two grades of the same polymer grade, Sumikasuper: GF15 (15% glass-fiber reinforced) versus GF30 (30% glass-fiber reinforced). The chemistry is identical, so every difference below comes from the condition. Sumikasuper GF30 is the stronger of the two: tensile strength 160 MPa (23.2 ksi) against 150 MPa (21.8 ksi) for Sumikasuper GF15, about 7% more. In exchange, Sumikasuper GF15 is the more ductile: elongation 2.6% versus 2.2% for Sumikasuper GF30. Sumikasuper GF15 is lighter (1.52 g/cm³ vs 1.62 g/cm³ for Sumikasuper GF30) and Sumikasuper GF30 is stiffer (14 GPa vs 11 GPa).
Sumikasuper GF15Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
Sumikasuper GF30Choose it when strength drives the design.
Sumikasuper GF15 vs Sumikasuper GF30: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Sumikasuper GF15Sumikasuper GF30
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Flexural Strength
Flexural Modulus
Izod Impact, Notched
Same in both: Poisson's Ratio 0.35 · Compressive Strength 120 MPa17.4 ksi · Hardness, Shore D 88 Shore D · Hardness, Rockwell M 90 HRM
Physical
Density and transition temperatures.
Density
Same in both: Melting Temperature (Tm) 335°C635 °F · Glass Transition (Tg) 120°C248 °F · Water Absorption (24 h) 0.02% · Water Absorption (Saturation) 0.05%
Thermal
How each material carries heat and how hot it can run.
Thermal Expansion (CTE, 20–100 °C)
Heat Deflection Temp. @ 1.8 MPa
Same in both: Thermal Conductivity 0.5 W/m·K0.29 BTU/hr·ft·°F · Specific Heat Capacity 1,100 J/kg·K0.26 BTU/lb·°F · Max Service Temperature (continuous) 220°C428 °F · Min Service Temperature -50°C-58 °F · Heat Deflection Temp. @ 0.45 MPa 290°C554 °F · Limiting Oxygen Index 40% · Max Service Temperature (short-term) 300°C572 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 1×10¹³ Ω·m3.94×10²⁰ µΩ·in · Dielectric Strength 40 kV/mm1,016 V/mil · Dielectric Constant (1 MHz) 3.9 · Dissipation Factor (1 MHz) 0.003 · Volume Resistivity 1×10¹⁵ Ω·cm · Surface Resistivity 1×10¹⁵ Ω · Comparative Tracking Index (CTI) 200 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 90 / 100 · UV / Weathering Resistance 35 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Mold Shrinkage
Same in both: Machinability 45 / 100 · Weldability 30 / 100 · Formability (cold) 20 / 100 · Polishability 40 / 100 · Melt Flow Rate 25 g/10 min · Processing Melt Temperature (typ.) 350°C662 °F · Mold Temperature (typ.) 110°C230 °F
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 160 MJ/kg68,788 BTU/lb · Embodied Carbon (primary production) 8.5 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Sumikasuper GF15 vs Sumikasuper GF30 — frequently asked
Is Sumikasuper GF30 stronger than Sumikasuper GF15?
Yes. Sumikasuper GF30 has a typical tensile strength of 160 MPa (23.2 ksi) against 150 MPa (21.8 ksi) for Sumikasuper GF15 — about 7% more.
Which grade does FabDigit quote by default, GF15 or GF30?
GF30 is the default Sumikasuper condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose Sumikasuper GF15 over Sumikasuper GF30?
Pick Sumikasuper GF15 when the part is bent, formed or impact-loaded, or when weight is the constraint. Pick Sumikasuper GF30 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Sumikasuper GF15 and Sumikasuper GF30 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.