PP-C vs PP-H
Polymer · grade comparison
PP-C and PP-H are both polymer grades. PP-H is the stronger of the two: yield strength 34 MPa (4.93 ksi) against 25 MPa (3.63 ksi) for PP-C, about 36% more; tensile strength follows at 35 MPa (5.08 ksi) vs 26 MPa (3.77 ksi). In exchange, PP-C is the more ductile: elongation 350% versus 300% for PP-H, and PP-H is harder (72 Shore D vs 67 Shore D). PP-H is stiffer (1.5 GPa vs 1.1 GPa).
PP-CChoose it when the part is bent, formed or impact-loaded.
PP-HChoose it when strength drives the design.
PP-C vs PP-H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Fracture Toughness (K_IC)
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell R
Hardness, Rockwell M
Physical
Density and transition temperatures.
Density
Melting Temperature (Tm)
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Same in both: Refractive Index 1.49
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Min Service Temperature
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Max Service Temperature (short-term)
Same in both: Specific Heat Capacity 1,900 J/kg·K0.45 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 110 µm/m·K61.1 µin/in·°F · Limiting Oxygen Index 18%
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dissipation Factor (1 MHz)
Volume Resistivity
Same in both: Dielectric Constant (1 MHz) 2.25 · Surface Resistivity 1×10¹⁵ Ω · Comparative Tracking Index (CTI) 600 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
UV / Weathering Resistance
Same in both: Corrosion Resistance 90 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Polishability
Mold Shrinkage
Mold Temperature (typ.)
Same in both: Machinability 65 / 100 · Melt Flow Rate 12 g/10 min · Processing Melt Temperature (typ.) 230°C446 °F
Sustainability
Primary-production footprint per kilogram.
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 78 MJ/kg33,534 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Same in both: Thermal Diffusivity 0.1 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | PP-C | PP-H |
|---|---|---|
| Default condition | — | — |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
PP-C vs PP-H — frequently asked
Is PP-H stronger than PP-C?
Yes. PP-H has a typical yield strength of 34 MPa (4.93 ksi) against 25 MPa (3.63 ksi) for PP-C — about 36% more. Tensile strength is 35 MPa (5.08 ksi) vs 26 MPa (3.77 ksi).
Which is cheaper, PP-C or PP-H?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose PP-C over PP-H?
Pick PP-C when the part is bent, formed or impact-loaded. Pick PP-H when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in PP-C and PP-H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.