PC-Medical GF30 vs PC-Medical IM
Polymer · PC-Medical grade comparison
PC-Medical GF30 and PC-Medical IM are two grades of the same polymer grade, PC-Medical: GF30 (30% glass-fiber reinforced medical PC) versus IM (impact-modified / low-temperature-toughened medical PC). The chemistry is identical, so every difference below comes from the condition. PC-Medical GF30 is the stronger of the two: yield strength 62 MPa (8.99 ksi) against 55 MPa (7.98 ksi) for PC-Medical IM, about 13% more; tensile strength follows at 125 MPa (18.1 ksi) vs 60 MPa (8.7 ksi). In exchange, PC-Medical IM is the more ductile: elongation 130% versus 3% for PC-Medical GF30. PC-Medical IM is lighter (1.2 g/cm³ vs 1.43 g/cm³ for PC-Medical GF30) and PC-Medical GF30 is stiffer (7.5 GPa vs 2.1 GPa). On the shop floor, PC-Medical IM machines more easily (good vs fair) and PC-Medical GF30 welds better (very good vs fair).
PC-Medical GF30Choose it when strength drives the design, or when it will be welded.
PC-Medical IMChoose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
PC-Medical GF30 vs PC-Medical IM: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Flexural Strength
Flexural Modulus
Shear Strength
Fracture Toughness (K_IC)
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell M
Hardness, Rockwell R
Same in both: Shear Modulus 0.85 GPa0.12 Msi · Bulk Modulus 3 GPa0.49 Msi · Poisson's Ratio 0.37 · Compressive Modulus 2.4 GPa0.35 Msi
Physical
Density and transition temperatures.
Density
Light Transmission
Same in both: Glass Transition (Tg) 147°C297 °F · Water Absorption (24 h) 0.15% · Water Absorption (Saturation) 0.35% · Refractive Index 1.586
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Limiting Oxygen Index
Same in both: Specific Heat Capacity 1,200 J/kg·K0.29 BTU/lb·°F · Max Service Temperature (short-term) 145°C293 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 1×10¹⁴ Ω·m3.94×10²¹ µΩ·in · Dielectric Strength 25 kV/mm635 V/mil · Dielectric Constant (1 MHz) 2.9 · Dissipation Factor (1 MHz) 0.01 · Volume Resistivity 1×10¹⁶ Ω·cm · Surface Resistivity 1×10¹⁵ Ω · Comparative Tracking Index (CTI) 250 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: UV / Weathering Resistance 30 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Mold Shrinkage
Melt Flow Rate
Same in both: Polishability 90 / 100 · Processing Melt Temperature (typ.) 300°C572 °F · Mold Temperature (typ.) 95°C203 °F
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 105 MJ/kg45,142 BTU/lb · Embodied Carbon (primary production) 6 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PC-Medical GF30 vs PC-Medical IM — frequently asked
Is PC-Medical GF30 stronger than PC-Medical IM?
Yes. PC-Medical GF30 has a typical yield strength of 62 MPa (8.99 ksi) against 55 MPa (7.98 ksi) for PC-Medical IM — about 13% more. Tensile strength is 125 MPa (18.1 ksi) vs 60 MPa (8.7 ksi).
Which grade does FabDigit quote by default, GF30 or IM?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, PC-Medical GF30 or PC-Medical IM?
PC-Medical IM. Its machinability rates good (58/100) against fair (40/100) for PC-Medical GF30; for welding the order is PC-Medical GF30 first (very good, 75/100) then PC-Medical IM (fair, 40/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in PC-Medical GF30 and PC-Medical IM side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.