PAS GF10 vs PAS GF30
Polymer · PAS grade comparison
PAS GF10 and PAS GF30 are two grades of the same polymer grade, PAS: GF10 (10 % glass-fibre reinforced) versus GF30 (30 % glass-fibre reinforced). The chemistry is identical, so every difference below comes from the condition. PAS GF30 is the stronger of the two: yield strength 140 MPa (20.3 ksi) against 75 MPa (10.9 ksi) for PAS GF10, about 87% more; tensile strength follows at 140 MPa (20.3 ksi) vs 92 MPa (13.3 ksi). In exchange, PAS GF10 is the more ductile: elongation 6% versus 2.5% for PAS GF30. PAS GF10 is lighter (1.36 g/cm³ vs 1.51 g/cm³ for PAS GF30) and PAS GF30 is stiffer (9 GPa vs 4 GPa). On the shop floor, PAS GF10 machines more easily (good vs fair).
PAS GF10Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
PAS GF30Choose it when strength drives the design.
PAS GF10 vs PAS GF30: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Flexural Strength
Flexural Modulus
Izod Impact, Notched
Same in both: Shear Modulus 0.9 GPa0.13 Msi · Poisson's Ratio 0.4 · Compressive Strength 100 MPa14.5 ksi · Compressive Modulus 2.5 GPa0.36 Msi · Shear Strength 62 MPa9 ksi · Fracture Toughness (K_IC) 2.6 MPa·√m2.4 ksi·√in · Hardness, Shore A 96 Shore A · Hardness, Shore D 85 Shore D · Hardness, Rockwell M 88 HRM · Hardness, Rockwell R 120 HRR
Physical
Density and transition temperatures.
Density
Light Transmission
Same in both: Glass Transition (Tg) 210°C410 °F · Water Absorption (24 h) 0.4% · Water Absorption (Saturation) 1.2% · Refractive Index 1.64
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Heat Deflection Temp. @ 1.8 MPa
Same in both: Specific Heat Capacity 1,150 J/kg·K0.27 BTU/lb·°F · Min Service Temperature -100°C-148 °F · Heat Deflection Temp. @ 0.45 MPa 195°C383 °F · Vicat Softening Point (B50) 210°C410 °F · Limiting Oxygen Index 34% · Max Service Temperature (short-term) 210°C410 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 1×10¹⁴ Ω·m3.94×10²¹ µΩ·in · Dielectric Strength 17 kV/mm432 V/mil · Dielectric Constant (1 MHz) 3.4 · Dissipation Factor (1 MHz) 0.008 · Volume Resistivity 1×10¹⁶ Ω·cm · Surface Resistivity 1×10¹⁵ Ω · Comparative Tracking Index (CTI) 150 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 85 / 100 · UV / Weathering Resistance 30 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Mold Shrinkage
Same in both: Weldability 72 / 100 · Formability (cold) 60 / 100 · Polishability 70 / 100 · Melt Flow Rate 20 g/10 min · Processing Melt Temperature (typ.) 360°C680 °F · Mold Temperature (typ.) 150°C302 °F
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 145 MJ/kg62,339 BTU/lb · Embodied Carbon (primary production) 8 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PAS GF10 vs PAS GF30 — frequently asked
Is PAS GF30 stronger than PAS GF10?
Yes. PAS GF30 has a typical yield strength of 140 MPa (20.3 ksi) against 75 MPa (10.9 ksi) for PAS GF10 — about 87% more. Tensile strength is 140 MPa (20.3 ksi) vs 92 MPa (13.3 ksi).
Which grade does FabDigit quote by default, GF10 or GF30?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, PAS GF10 or PAS GF30?
PAS GF10. Its machinability rates good (55/100) against fair (45/100) for PAS GF30.
Ready to make it?
Upload a CAD file and FabDigit prices the part in PAS GF10 and PAS GF30 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.