PA612 GF15 vs PA612 GF50
Polymer · PA612 grade comparison
PA612 GF15 and PA612 GF50 are two grades of the same polymer grade, PA612: GF15 (15 % glass-fibre reinforced) versus GF50 (50 % glass-fibre reinforced). The chemistry is identical, so every difference below comes from the condition. PA612 GF50 is the stronger of the two: tensile strength 195 MPa (28.3 ksi) against 105 MPa (15.2 ksi) for PA612 GF15, about 86% more. In exchange, PA612 GF15 is the more ductile: elongation 6% versus 2.5% for PA612 GF50. PA612 GF15 is lighter (1.18 g/cm³ vs 1.55 g/cm³ for PA612 GF50) and PA612 GF50 is stiffer (15 GPa vs 4.8 GPa). On the shop floor, PA612 GF15 machines more easily (good vs fair).
PA612 GF15Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
PA612 GF50Choose it when strength drives the design.
PA612 GF15 vs PA612 GF50: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Flexural Strength
Flexural Modulus
Izod Impact, Notched
Same in both: Shear Modulus 0.78 GPa0.11 Msi · Bulk Modulus 4 GPa0.51 Msi · Poisson's Ratio 0.39 · Yield Strength (0.2% offset) 58 MPa8.4 ksi · Compressive Strength 60 MPa8.7 ksi · Compressive Modulus 2 GPa0.29 Msi · Shear Strength 50 MPa7.3 ksi · Hardness, Shore D 79 Shore D · Hardness, Rockwell M 78 HRM · Hardness, Rockwell R 115 HRR
Physical
Density and transition temperatures.
Density
Same in both: Melting Temperature (Tm) 218°C424 °F · Glass Transition (Tg) 48°C118 °F · Water Absorption (24 h) 0.3% · Water Absorption (Saturation) 2.7% · Refractive Index 1.53
Thermal
How each material carries heat and how hot it can run.
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Heat Deflection Temp. @ 1.8 MPa
Same in both: Thermal Conductivity 0.22 W/m·K0.13 BTU/hr·ft·°F · Specific Heat Capacity 1,700 J/kg·K0.41 BTU/lb·°F · Min Service Temperature -40°C-40 °F · Heat Deflection Temp. @ 0.45 MPa 160°C320 °F · Vicat Softening Point (B50) 185°C365 °F · Limiting Oxygen Index 24% · Max Service Temperature (short-term) 160°C320 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 1×10¹² Ω·m3.94×10¹⁹ µΩ·in · Dielectric Strength 28 kV/mm711 V/mil · Dielectric Constant (1 MHz) 3.1 · Dissipation Factor (1 MHz) 0.02 · Volume Resistivity 1×10¹⁵ Ω·cm · Surface Resistivity 1×10¹⁴ Ω · Comparative Tracking Index (CTI) 600 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 72 / 100 · UV / Weathering Resistance 35 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Mold Shrinkage
Same in both: Weldability 70 / 100 · Formability (cold) 60 / 100 · Polishability 55 / 100 · Processing Melt Temperature (typ.) 260°C500 °F · Mold Temperature (typ.) 80°C176 °F
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 130 MJ/kg55,890 BTU/lb · Embodied Carbon (primary production) 7.5 kg CO₂/kg · Embodied Water 350 L/kg41.9 gal/lb · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PA612 GF15 vs PA612 GF50 — frequently asked
Is PA612 GF50 stronger than PA612 GF15?
Yes. PA612 GF50 has a typical tensile strength of 195 MPa (28.3 ksi) against 105 MPa (15.2 ksi) for PA612 GF15 — about 86% more.
Which grade does FabDigit quote by default, GF15 or GF50?
NAT-DAM is the default PA612 condition in the FabDigit quote flow (neither GF15 nor GF50). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, PA612 GF15 or PA612 GF50?
PA612 GF15. Its machinability rates good (55/100) against fair (35/100) for PA612 GF50.
Ready to make it?
Upload a CAD file and FabDigit prices the part in PA612 GF15 and PA612 GF50 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.