PA6/66 GF15 vs PA6/66 GF30
Polymer · PA6/66 grade comparison
PA6/66 GF15 and PA6/66 GF30 are two grades of the same polymer grade, PA6/66: GF15 (15% short glass fiber reinforced) versus GF30 (30% short glass fiber reinforced). The chemistry is identical, so every difference below comes from the condition. PA6/66 GF30 is the stronger of the two: tensile strength 175 MPa (25.4 ksi) against 115 MPa (16.7 ksi) for PA6/66 GF15, about 52% more. In exchange, PA6/66 GF15 is the more ductile: elongation 5% versus 3.2% for PA6/66 GF30. PA6/66 GF15 is lighter (1.23 g/cm³ vs 1.36 g/cm³ for PA6/66 GF30) and PA6/66 GF30 is stiffer (9.5 GPa vs 5.5 GPa). On the shop floor, PA6/66 GF15 machines more easily (52 vs 42 out of 100) and PA6/66 GF15 welds better (very good vs good).
PA6/66 GF15Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
PA6/66 GF30Choose it when strength drives the design, or when the part sees heat.
PA6/66 GF15 vs PA6/66 GF30: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Flexural Strength
Flexural Modulus
Izod Impact, Notched
Hardness, Rockwell M
Same in both: Shear Modulus 1 GPa0.15 Msi · Poisson's Ratio 0.39 · Yield Strength (0.2% offset) 72 MPa10.4 ksi · Compressive Strength 80 MPa11.6 ksi · Shear Strength 55 MPa8 ksi · Hardness, Shore D 80 Shore D · Hardness, Rockwell R 118 HRR
Physical
Density and transition temperatures.
Density
Same in both: Melting Temperature (Tm) 196°C385 °F · Glass Transition (Tg) 50°C122 °F · Water Absorption (24 h) 1.8% · Water Absorption (Saturation) 9.5%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Same in both: Specific Heat Capacity 1,700 J/kg·K0.41 BTU/lb·°F · Min Service Temperature -40°C-40 °F · Vicat Softening Point (B50) 180°C356 °F · Limiting Oxygen Index 24% · Max Service Temperature (short-term) 150°C302 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 1×10¹² Ω·m3.94×10¹⁹ µΩ·in · Dielectric Strength 25 kV/mm635 V/mil · Dielectric Constant (1 MHz) 3.4 · Dissipation Factor (1 MHz) 0.03 · Volume Resistivity 1×10¹⁴ Ω·cm · Surface Resistivity 1×10¹³ Ω · Comparative Tracking Index (CTI) 600 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 60 / 100 · UV / Weathering Resistance 30 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Mold Shrinkage
Same in both: Formability (cold) 60 / 100 · Polishability 55 / 100 · Melt Flow Rate 25 g/10 min · Processing Melt Temperature (typ.) 260°C500 °F · Mold Temperature (typ.) 70°C158 °F
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 122 MJ/kg52,451 BTU/lb · Embodied Carbon (primary production) 7.5 kg CO₂/kg · Embodied Water 450 L/kg53.9 gal/lb · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PA6/66 GF15 vs PA6/66 GF30 — frequently asked
Is PA6/66 GF30 stronger than PA6/66 GF15?
Yes. PA6/66 GF30 has a typical tensile strength of 175 MPa (25.4 ksi) against 115 MPa (16.7 ksi) for PA6/66 GF15 — about 52% more.
Which grade does FabDigit quote by default, GF15 or GF30?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, PA6/66 GF15 or PA6/66 GF30?
PA6/66 GF15, by a small margin. Both rate fair for machinability — 52/100 against 42/100 for PA6/66 GF30; for welding the order is PA6/66 GF15 first (very good, 78/100) then PA6/66 GF30 (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in PA6/66 GF15 and PA6/66 GF30 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.