PA11 EOS PA 1101 vs PA11 Sinterit PA11 CF
Polymer · PA11 grade comparison
EOS PA 1101 and Sinterit PA11 CF are two grades of the same polymer grade, PA11: EOS PA 1101 versus Sinterit PA11 CF. The chemistry is identical, so every difference below comes from the condition. Sinterit PA11 CF is the stronger of the two: tensile strength 81 MPa (11.7 ksi) against 50 MPa (7.25 ksi) for EOS PA 1101, about 62% more. In exchange, EOS PA 1101 is the more ductile: elongation 30% versus 24.5% for Sinterit PA11 CF, and Sinterit PA11 CF is harder (81 Shore D vs 75 Shore D). EOS PA 1101 is lighter (1.03 g/cm³ vs 1.09 g/cm³ for Sinterit PA11 CF) and Sinterit PA11 CF is stiffer (2.95 GPa vs 1.65 GPa).
EOS PA 1101Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
Sinterit PA11 CFChoose it when strength drives the design.
EOS PA 1101 vs Sinterit PA11 CF: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Charpy Impact, Notched (ISO 179)
Hardness, Shore D
Flexural Strength
Flexural Modulus
Charpy Impact, Unnotched (ISO 179)
Physical
Density and transition temperatures.
Melting Temperature (Tm)
Density
Water Absorption (24 h)
Thermal
How each material carries heat and how hot it can run.
Heat Deflection Temp. @ 1.8 MPa
Heat Deflection Temp. @ 0.45 MPa
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Powder Bulk Density
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
EOS PA 1101 vs Sinterit PA11 CF — frequently asked
Is Sinterit PA11 CF stronger than EOS PA 1101?
Yes. Sinterit PA11 CF has a typical tensile strength of 81 MPa (11.7 ksi) against 50 MPa (7.25 ksi) for EOS PA 1101 — about 62% more.
Which grade does FabDigit quote by default, EOS PA 1101 or Sinterit PA11 CF?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
When should I choose EOS PA 1101 over Sinterit PA11 CF?
Pick EOS PA 1101 when the part is bent, formed or impact-loaded, or when weight is the constraint. Pick Sinterit PA11 CF when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in EOS PA 1101 and Sinterit PA11 CF side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.