Aurum PD450 ESD vs Aurum PD450 GF30
Polymer · Aurum PD450 grade comparison
Aurum PD450 ESD and Aurum PD450 GF30 are two grades of the same polymer grade, Aurum PD450: ESD (ESD / static-dissipative carbon-filled grade) versus GF30 (30% glass-fiber reinforced). The chemistry is identical, so every difference below comes from the condition. Aurum PD450 GF30 is the stronger of the two: tensile strength 165 MPa (23.9 ksi) against 110 MPa (16 ksi) for Aurum PD450 ESD, about 50% more. In exchange, Aurum PD450 ESD is the more ductile: elongation 3% versus 2.5% for Aurum PD450 GF30. Aurum PD450 ESD is lighter (1.42 g/cm³ vs 1.55 g/cm³ for Aurum PD450 GF30) and Aurum PD450 GF30 is stiffer (9.5 GPa vs 6.5 GPa). On the shop floor, Aurum PD450 GF30 welds better (45 vs 35 out of 100).
Aurum PD450 ESDChoose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
Aurum PD450 GF30Choose it when strength drives the design, or when it will be welded.
Aurum PD450 ESD vs Aurum PD450 GF30: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Aurum PD450 ESDAurum PD450 GF30
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Flexural Modulus
Izod Impact, Notched
Hardness, Rockwell M
Same in both: Poisson's Ratio 0.4 · Yield Strength (0.2% offset) 90 MPa13.1 ksi
Physical
Density and transition temperatures.
Density
Same in both: Melting Temperature (Tm) 388°C730 °F · Glass Transition (Tg) 250°C482 °F · Water Absorption (24 h) 0.24% · Water Absorption (Saturation) 1%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Limiting Oxygen Index
Same in both: Specific Heat Capacity 1,150 J/kg·K0.27 BTU/lb·°F · Min Service Temperature -196°C-321 °F · Max Service Temperature (short-term) 300°C572 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Volume Resistivity
Surface Resistivity
Same in both: Dielectric Strength 22 kV/mm559 V/mil · Dielectric Constant (1 MHz) 3.3 · Dissipation Factor (1 MHz) 0.002 · Comparative Tracking Index (CTI) 175 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: UV / Weathering Resistance 55 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Mold Shrinkage
Same in both: Polishability 70 / 100 · Processing Melt Temperature (typ.) 410°C770 °F · Mold Temperature (typ.) 200°C392 °F
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 320 MJ/kg137,575 BTU/lb · Embodied Carbon (primary production) 16 kg CO₂/kg · Embodied Water 600 L/kg71.9 gal/lb · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Aurum PD450 ESD vs Aurum PD450 GF30 — frequently asked
Is Aurum PD450 GF30 stronger than Aurum PD450 ESD?
Yes. Aurum PD450 GF30 has a typical tensile strength of 165 MPa (23.9 ksi) against 110 MPa (16 ksi) for Aurum PD450 ESD — about 50% more.
Which grade does FabDigit quote by default, ESD or GF30?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, Aurum PD450 ESD or Aurum PD450 GF30?
Aurum PD450 ESD, by a small margin. Both rate fair for machinability — 50/100 against 45/100 for Aurum PD450 GF30; for welding the order is Aurum PD450 GF30 first (fair, 45/100) then Aurum PD450 ESD (fair, 35/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Aurum PD450 ESD and Aurum PD450 GF30 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.