Nickel Alloy Invar 36-CD vs Invar 36-HR
Nickel Alloy · Invar 36 temper comparison
Invar 36-CD and Invar 36-HR are two conditions of the same nickel alloy grade, Invar 36: CD (cold drawn) versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. Invar 36-CD is the stronger of the two: yield strength 560 MPa (81.2 ksi) against 300 MPa (43.5 ksi) for Invar 36-HR, about 87% more; tensile strength follows at 700 MPa (102 ksi) vs 500 MPa (72.5 ksi). In exchange, Invar 36-HR is the more ductile: elongation 35% versus 15% for Invar 36-CD, and Invar 36-CD is harder (210 HB vs 150 HB).
Invar 36-CDChoose it when strength drives the design.
Invar 36-HRChoose it when the part is bent, formed or impact-loaded.
Invar 36-CD vs Invar 36-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 55 GPa8 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 8.1 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,427°C2,601 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Expansion (CTE, 20–100 °C)
Same in both: Thermal Conductivity 10.5 W/m·K6.1 BTU/hr·ft·°F · Specific Heat Capacity 515 J/kg·K0.12 BTU/lb·°F · Latent Heat of Fusion 275 J/g118 BTU/lb · Max Service Temperature (continuous) 230°C446 °F · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.1 % IACS · Electrical Resistivity 8.2×10⁻⁷ Ω·m32.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.35 V · Corrosion Resistance 32 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Machinability 30 / 100 · Weldability 70 / 100 · Castability 40 / 100 · Brazeability / Solderability 65 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 90 MJ/kg38,693 BTU/lb · Embodied Carbon (primary production) 6.5 kg CO₂/kg · Embodied Water 180 L/kg21.6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Invar 36-CD vs Invar 36-HR — frequently asked
Is Invar 36-CD stronger than Invar 36-HR?
Yes. Invar 36-CD has a typical yield strength of 560 MPa (81.2 ksi) against 300 MPa (43.5 ksi) for Invar 36-HR — about 87% more. Tensile strength is 700 MPa (102 ksi) vs 500 MPa (72.5 ksi).
Which condition does FabDigit quote by default, CD or HR?
O is the default Invar 36 condition in the FabDigit quote flow (neither CD nor HR). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose Invar 36-CD over Invar 36-HR?
Pick Invar 36-CD when strength drives the design. Pick Invar 36-HR when the part is bent, formed or impact-loaded.