Nickel Alloy Inconel 718 Cold Drawn vs Inconel 718 Hot Rolled
Nickel Alloy · Inconel 718 temper comparison
Inconel 718 Cold Drawn and Inconel 718 Hot Rolled are two conditions of the same nickel alloy grade, Inconel 718: Cold Drawn versus Hot Rolled. The chemistry is identical, so every difference below comes from the condition. Inconel 718 Cold Drawn is the stronger of the two: yield strength 1,050 MPa (152 ksi) against 700 MPa (102 ksi) for Inconel 718 Hot Rolled, about 50% more; tensile strength follows at 1,250 MPa (181 ksi) vs 1,050 MPa (152 ksi). In exchange, Inconel 718 Hot Rolled is the more ductile: elongation 30% versus 12% for Inconel 718 Cold Drawn, and Inconel 718 Cold Drawn is harder (353 HB vs 260 HB). Inconel 718 Hot Rolled runs hotter in service (650°C vs 540°C continuous).
Inconel 718 Cold DrawnChoose it when strength drives the design.
Inconel 718 Hot RolledChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Inconel 718 Cold Drawn vs Inconel 718 Hot Rolled: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Inconel 718 Cold DrawnInconel 718 Hot Rolled
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 163 GPa23.6 Msi · Poisson's Ratio 0.29 · Hardness, Rockwell B 92 HRB
Physical
Density and transition temperatures.
Same in both: Density 8.19 g/cm³0.3 lb/in³ · Melting Point (Solidus) 1,260°C2,300 °F · Liquidus Temperature 1,336°C2,437 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 11.4 W/m·K6.6 BTU/hr·ft·°F · Specific Heat Capacity 435 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 13 µm/m·K7.2 µin/in·°F · Latent Heat of Fusion 210 J/g90.3 BTU/lb · Min Service Temperature -253°C-423 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 1.4 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 45 / 100 · Brazeability / Solderability 55 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 250 MJ/kg107,481 BTU/lb · Embodied Carbon (primary production) 16 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Inconel 718 Cold Drawn vs Inconel 718 Hot Rolled — frequently asked
Is Inconel 718 Cold Drawn stronger than Inconel 718 Hot Rolled?
Yes. Inconel 718 Cold Drawn has a typical yield strength of 1,050 MPa (152 ksi) against 700 MPa (102 ksi) for Inconel 718 Hot Rolled — about 50% more. Tensile strength is 1,250 MPa (181 ksi) vs 1,050 MPa (152 ksi).
Which condition does FabDigit quote by default, Cold Drawn or Hot Rolled?
Solution Annealed is the default Inconel 718 condition in the FabDigit quote flow (neither Cold Drawn nor Hot Rolled). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, Inconel 718 Cold Drawn or Inconel 718 Hot Rolled?
Inconel 718 Hot Rolled. Its weldability rates good (62/100) against good (55/100) for Inconel 718 Cold Drawn.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Inconel 718 Cold Drawn and Inconel 718 Hot Rolled side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.