Nickel Alloy 2.4878 +AT vs 2.4878 +P1100
Nickel Alloy · 2.4878 temper comparison
2.4878 +AT and 2.4878 +P1100 are two conditions of the same nickel alloy grade, 2.4878: +AT (solution annealed) versus +P1100 (precipitation hardened). The chemistry is identical, so every difference below comes from the condition. 2.4878 +P1100 is the stronger of the two: yield strength 760 MPa (110 ksi) against 450 MPa (65.3 ksi) for 2.4878 +AT, about 69% more; tensile strength follows at 1,190 MPa (173 ksi) vs 900 MPa (131 ksi). In exchange, 2.4878 +AT is the more ductile: elongation 40% versus 20% for 2.4878 +P1100, and 2.4878 +P1100 is harder (325 HB vs 220 HB). On the shop floor, 2.4878 +AT welds better (fair vs poor).
2.4878 +ATChoose it when the part is bent, formed or impact-loaded, or when it will be welded.
2.4878 +P1100Choose it when strength drives the design.
2.4878 +AT vs 2.4878 +P1100: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 213 GPa30.9 Msi · Shear Modulus 82 GPa11.9 Msi · Bulk Modulus 175 GPa25.4 Msi · Poisson's Ratio 0.3 · Compressive Strength 830 MPa120 ksi
Physical
Density and transition temperatures.
Same in both: Density 8.2 g/cm³0.3 lb/in³ · Melting Point (Solidus) 1,310°C2,390 °F · Liquidus Temperature 1,370°C2,498 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 11 W/m·K6.4 BTU/hr·ft·°F · Specific Heat Capacity 435 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 295 J/g127 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.4 % IACS · Electrical Resistivity 1.24×10⁻⁶ Ω·m48.8 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 45 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 150 MJ/kg64,488 BTU/lb · Embodied Carbon (primary production) 13 kg CO₂/kg · Embodied Water 400 L/kg47.9 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
2.4878 +AT vs 2.4878 +P1100 — frequently asked
Is 2.4878 +P1100 stronger than 2.4878 +AT?
Yes. 2.4878 +P1100 has a typical yield strength of 760 MPa (110 ksi) against 450 MPa (65.3 ksi) for 2.4878 +AT — about 69% more. Tensile strength is 1,190 MPa (173 ksi) vs 900 MPa (131 ksi).
Which condition does FabDigit quote by default, +AT or +P1100?
+P1080 is the default 2.4878 condition in the FabDigit quote flow (neither +AT nor +P1100). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 2.4878 +AT or 2.4878 +P1100?
2.4878 +AT, by a small margin. Both rate poor for machinability — 20/100 against 15/100 for 2.4878 +P1100; for welding the order is 2.4878 +AT first (fair, 45/100) then 2.4878 +P1100 (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2.4878 +AT and 2.4878 +P1100 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.