Magnesium Alloy ZE41A-F vs ZE41A-T5
Magnesium Alloy · ZE41A temper comparison
ZE41A-F and ZE41A-T5 are two conditions of the same magnesium alloy grade, ZE41A: F (as fabricated) versus T5 (cooled from hot working and artificially aged). The chemistry is identical, so every difference below comes from the condition. ZE41A-T5 is the stronger of the two: yield strength 140 MPa (20.3 ksi) against 115 MPa (16.7 ksi) for ZE41A-F, about 22% more; tensile strength follows at 205 MPa (29.7 ksi) vs 175 MPa (25.4 ksi). ZE41A-T5 is the more ductile: elongation 3.5% versus 3% for ZE41A-F, and ZE41A-T5 is harder (62 HB vs 55 HB). ZE41A-T5 runs hotter in service (150°C vs 120°C continuous).
ZE41A-T5Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
ZE41A-F vs ZE41A-T5: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 44 GPa6.4 Msi · Shear Modulus 16.5 GPa2.4 Msi · Bulk Modulus 45 GPa6.5 Msi · Poisson's Ratio 0.35 · Fracture Toughness (K_IC) 13 MPa·√m11.8 ksi·√in · Charpy V-Notch Impact (RT) 4 J3 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 1.84 g/cm³0.07 lb/in³ · Melting Point (Solidus) 510°C950 °F · Liquidus Temperature 645°C1,193 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 1,000 J/kg·K0.24 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 26.1 µm/m·K14.5 µin/in·°F · Latent Heat of Fusion 350 J/g150 BTU/lb · Min Service Temperature -70°C-94 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -1.6 V · Corrosion Resistance 22 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Same in both: Machinability Rating (AISI 1212 = 100 %) 500% · Formability (cold) 10 / 100 · Castability 92 / 100 · Brazeability / Solderability 20 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 340 MJ/kg146,174 BTU/lb · Embodied Carbon (primary production) 28 kg CO₂/kg · Embodied Water 500 L/kg59.9 gal/lb · Typical Recycled Content 15%
Strength versus weight
Yield strength against density for every magnesium alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
ZE41A-F vs ZE41A-T5 — frequently asked
Is ZE41A-T5 stronger than ZE41A-F?
Yes. ZE41A-T5 has a typical yield strength of 140 MPa (20.3 ksi) against 115 MPa (16.7 ksi) for ZE41A-F — about 22% more. Tensile strength is 205 MPa (29.7 ksi) vs 175 MPa (25.4 ksi).
Which condition does FabDigit quote by default, F or T5?
T5 is the default ZE41A condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose ZE41A-F over ZE41A-T5?
Pick ZE41A-T5 when strength drives the design, or when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in ZE41A-F and ZE41A-T5 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.