Magnesium Alloy QE22 HIP+T6 vs QE22-T4
Magnesium Alloy · QE22 temper comparison
QE22 HIP+T6 and QE22-T4 are two conditions of the same magnesium alloy grade, QE22: HIP+T6 versus T4 (solution heat treated and naturally aged). The chemistry is identical, so every difference below comes from the condition. QE22 HIP+T6 is the stronger of the two: yield strength 200 MPa (29 ksi) against 115 MPa (16.7 ksi) for QE22-T4, about 74% more; tensile strength follows at 270 MPa (39.2 ksi) vs 220 MPa (31.9 ksi). In exchange, QE22-T4 is the more ductile: elongation 6% versus 5% for QE22 HIP+T6, and QE22 HIP+T6 is harder (80 HB vs 60 HB). QE22 HIP+T6 runs hotter in service (200°C vs 150°C continuous) and QE22 HIP+T6 conducts heat better (113 W/m·K vs 100 W/m·K).
QE22 HIP+T6Choose it when strength drives the design, or when the part sees heat.
QE22-T4Choose it when the part is bent, formed or impact-loaded.
QE22 HIP+T6 vs QE22-T4: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 44 GPa6.4 Msi · Shear Modulus 16.5 GPa2.4 Msi · Bulk Modulus 45 GPa6.5 Msi · Poisson's Ratio 0.35
Physical
Density and transition temperatures.
Same in both: Density 1.82 g/cm³0.07 lb/in³ · Melting Point (Solidus) 549°C1,020 °F · Liquidus Temperature 604°C1,119 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 1,000 J/kg·K0.24 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 26.7 µm/m·K14.8 µin/in·°F · Latent Heat of Fusion 370 J/g159 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -1.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 75 / 100 · Brazeability / Solderability 15 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 380 MJ/kg163,371 BTU/lb · Embodied Carbon (primary production) 32 kg CO₂/kg · Embodied Water 500 L/kg59.9 gal/lb · Typical Recycled Content 15%
Strength versus weight
Yield strength against density for every magnesium alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
QE22 HIP+T6 vs QE22-T4 — frequently asked
Is QE22 HIP+T6 stronger than QE22-T4?
Yes. QE22 HIP+T6 has a typical yield strength of 200 MPa (29 ksi) against 115 MPa (16.7 ksi) for QE22-T4 — about 74% more. Tensile strength is 270 MPa (39.2 ksi) vs 220 MPa (31.9 ksi).
Which condition does FabDigit quote by default, HIP+T6 or T4?
T6 is the default QE22 condition in the FabDigit quote flow (neither HIP+T6 nor T4). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, QE22 HIP+T6 or QE22-T4?
QE22-T4. Its weldability rates good (60/100) against good (55/100) for QE22 HIP+T6.
Ready to make it?
Upload a CAD file and FabDigit prices the part in QE22 HIP+T6 and QE22-T4 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.