Magnesium Alloy AZ91D vs ZK61A
Magnesium Alloy · grade comparison
Magnesium Alloy AZ91D and ZK61A are both magnesium alloy grades. ZK61A is the stronger of the two: yield strength 195 MPa (28.3 ksi) against 160 MPa (23.2 ksi) for AZ91D, about 22% more; tensile strength follows at 310 MPa (45 ksi) vs 230 MPa (33.4 ksi). ZK61A is the more ductile: elongation 10% versus 3% for AZ91D, and ZK61A is harder (70 HB vs 63 HB). ZK61A conducts heat better (122 W/m·K vs 72 W/m·K). On the shop floor, AZ91D welds better (fair vs poor) and AZ91D sits in a lower cost tier (standard, $$) than ZK61A (premium, $$$).
AZ91DChoose it when it will be welded, or when cost is the deciding factor.
ZK61AChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
AZ91D vs ZK61A: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 45 GPa6.5 Msi · Shear Modulus 17 GPa2.5 Msi · Bulk Modulus 45 GPa6.5 Msi · Poisson's Ratio 0.35
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Max Service Temperature (continuous) 120°C248 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Castability
Brazeability / Solderability
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 400% · Formability (cold) 15 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 500 L/kg59.9 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every magnesium alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | AZ91D | ZK61A |
|---|---|---|
| CNC machining | Yes | — |
| Casting & forging | Yes | — |
| Default condition | As Cast | — |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Chem Film (Alodine) | Yes | — |
| E-Coating | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
AZ91D vs ZK61A — frequently asked
Is ZK61A stronger than AZ91D?
Yes. ZK61A has a typical yield strength of 195 MPa (28.3 ksi) against 160 MPa (23.2 ksi) for AZ91D — about 22% more. Tensile strength is 310 MPa (45 ksi) vs 230 MPa (33.4 ksi).
Which is cheaper, AZ91D or ZK61A?
AZ91D is the lower-cost material: it sits in the standard tier ($$) while ZK61A is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, AZ91D or ZK61A?
AZ91D. Its weldability rates fair (40/100) against poor (30/100) for ZK61A.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AZ91D and ZK61A side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.