Copper Alloy CC483K-GS vs CC483K-GZ
Copper Alloy · CC483K temper comparison
CC483K-GS and CC483K-GZ are two conditions of the same copper alloy grade, CC483K: GS (sand cast) versus GZ (centrifugally cast). The chemistry is identical, so every difference below comes from the condition. CC483K-GZ is the stronger of the two: yield strength 180 MPa (26.1 ksi) against 160 MPa (23.2 ksi) for CC483K-GS, about 13% more; tensile strength follows at 310 MPa (45 ksi) vs 280 MPa (40.6 ksi). CC483K-GZ is the more ductile: elongation 8% versus 7% for CC483K-GS, and CC483K-GZ is harder (98 HB vs 90 HB). CC483K-GZ is stiffer (100 GPa vs 95 GPa).
CC483K-GZChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
CC483K-GS vs CC483K-GZ: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 37 GPa5.4 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.75 g/cm³0.32 lb/in³ · Melting Point (Solidus) 830°C1,526 °F · Liquidus Temperature 1,000°C1,832 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.5 µm/m·K10.3 µin/in·°F · Latent Heat of Fusion 180 J/g77.4 BTU/lb · Max Service Temperature (continuous) 250°C482 °F · Min Service Temperature -180°C-292 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 9 % IACS · Electrical Resistivity 1.9×10⁻⁷ Ω·m7.48 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.27 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Weldability 25 / 100 · Formability (cold) 10 / 100 · Castability 75 / 100 · Brazeability / Solderability 70 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 62 MJ/kg26,655 BTU/lb · Embodied Carbon (primary production) 4.5 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 50%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
CC483K-GS vs CC483K-GZ — frequently asked
Is CC483K-GZ stronger than CC483K-GS?
Yes. CC483K-GZ has a typical yield strength of 180 MPa (26.1 ksi) against 160 MPa (23.2 ksi) for CC483K-GS — about 13% more. Tensile strength is 310 MPa (45 ksi) vs 280 MPa (40.6 ksi).
Which condition does FabDigit quote by default, GS or GZ?
GC is the default CC483K condition in the FabDigit quote flow (neither GS nor GZ). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose CC483K-GS over CC483K-GZ?
Pick CC483K-GZ when strength drives the design, or when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in CC483K-GS and CC483K-GZ side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.