Copper Alloy C97800-M06 vs C97800-M07
Copper Alloy · C97800 temper comparison
C97800-M06 and C97800-M07 are two conditions of the same copper alloy grade, C97800: M06 (as investment cast) versus M07 (as continuous cast). The chemistry is identical, so every difference below comes from the condition. C97800-M07 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 225 MPa (32.6 ksi) for C97800-M06, about 11% more; tensile strength follows at 435 MPa (63.1 ksi) vs 400 MPa (58 ksi). C97800-M07 is the more ductile: elongation 15% versus 13% for C97800-M06, and C97800-M07 is harder (140 HB vs 130 HB).
C97800-M07Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
C97800-M06 vs C97800-M07: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 47 GPa6.8 Msi · Bulk Modulus 118 GPa17.1 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 8.8 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,065°C1,949 °F · Liquidus Temperature 1,180°C2,156 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 25 W/m·K14.4 BTU/hr·ft·°F · Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.2 µm/m·K9 µin/in·°F · Latent Heat of Fusion 200 J/g86 BTU/lb · Max Service Temperature (continuous) 260°C500 °F · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 4.5 % IACS · Electrical Resistivity 3.83×10⁻⁷ Ω·m15.1 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Polishability
Same in both: Machinability 58 / 100 · Machinability Rating (AISI 1212 = 100 %) 60% · Weldability 25 / 100 · Formability (cold) 15 / 100 · Castability 65 / 100 · Brazeability / Solderability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 78 MJ/kg33,534 BTU/lb · Embodied Carbon (primary production) 5.6 kg CO₂/kg · Embodied Water 320 L/kg38.3 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C97800-M06 vs C97800-M07 — frequently asked
Is C97800-M07 stronger than C97800-M06?
Yes. C97800-M07 has a typical yield strength of 250 MPa (36.3 ksi) against 225 MPa (32.6 ksi) for C97800-M06 — about 11% more. Tensile strength is 435 MPa (63.1 ksi) vs 400 MPa (58 ksi).
Which condition does FabDigit quote by default, M06 or M07?
M01 is the default C97800 condition in the FabDigit quote flow (neither M06 nor M07). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C97800-M06 over C97800-M07?
Pick C97800-M07 when strength drives the design, or when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C97800-M06 and C97800-M07 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.