Copper Alloy C94500-M01 vs C94500-M07
Copper Alloy · C94500 temper comparison
C94500-M01 and C94500-M07 are two conditions of the same copper alloy grade, C94500: M01 (as sand cast) versus M07 (as continuous cast). The chemistry is identical, so every difference below comes from the condition. C94500-M07 is the stronger of the two: yield strength 90 MPa (13.1 ksi) against 83 MPa (12 ksi) for C94500-M01, about 8% more; tensile strength follows at 207 MPa (30 ksi) vs 172 MPa (24.9 ksi). In exchange, C94500-M01 is the more ductile: elongation 12% versus 10% for C94500-M07, and C94500-M07 is harder (55 HB vs 50 HB).
C94500-M01Choose it when the part is bent, formed or impact-loaded.
C94500-M07Choose it when strength drives the design.
C94500-M01 vs C94500-M07: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 76 GPa11 Msi · Shear Modulus 29 GPa4.2 Msi · Bulk Modulus 100 GPa14.5 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 762°C1,404 °F · Liquidus Temperature 943°C1,729 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 46.9 W/m·K27.1 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.5 µm/m·K10.3 µin/in·°F · Latent Heat of Fusion 165 J/g70.9 BTU/lb · Max Service Temperature (continuous) 230°C446 °F · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10 % IACS · Electrical Resistivity 1.72×10⁻⁷ Ω·m6.77 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.31 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Same in both: Machinability 88 / 100 · Machinability Rating (AISI 1212 = 100 %) 80% · Weldability 15 / 100 · Formability (cold) 8 / 100 · Castability 88 / 100 · Brazeability / Solderability 45 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 45 MJ/kg19,347 BTU/lb · Embodied Carbon (primary production) 3 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 75%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C94500-M01 vs C94500-M07 — frequently asked
Is C94500-M07 stronger than C94500-M01?
Yes. C94500-M07 has a typical yield strength of 90 MPa (13.1 ksi) against 83 MPa (12 ksi) for C94500-M01 — about 8% more. Tensile strength is 207 MPa (30 ksi) vs 172 MPa (24.9 ksi).
Which condition does FabDigit quote by default, M01 or M07?
M01 is the default C94500 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C94500-M01 over C94500-M07?
Pick C94500-M01 when the part is bent, formed or impact-loaded. Pick C94500-M07 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C94500-M01 and C94500-M07 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.