Copper Alloy C93900-M01 vs C93900-M07
Copper Alloy · C93900 temper comparison
C93900-M01 and C93900-M07 are two conditions of the same copper alloy grade, C93900: M01 (as sand cast) versus M07 (as continuous cast). The chemistry is identical, so every difference below comes from the condition. C93900-M07 is the stronger of the two: yield strength 152 MPa (22 ksi) against 138 MPa (20 ksi) for C93900-M01, about 10% more; tensile strength follows at 207 MPa (30 ksi) vs 193 MPa (28 ksi). In exchange, C93900-M01 is the more ductile: elongation 7% versus 5% for C93900-M07, and C93900-M07 is harder (70 HB vs 63 HB).
C93900-M01Choose it when the part is bent, formed or impact-loaded.
C93900-M07Choose it when strength drives the design.
C93900-M01 vs C93900-M07: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 76 GPa11 Msi · Shear Modulus 28 GPa4.1 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.78 g/cm³0.32 lb/in³ · Melting Point (Solidus) 762°C1,404 °F · Liquidus Temperature 943°C1,729 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 47 W/m·K27.2 BTU/hr·ft·°F · Specific Heat Capacity 251 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18 µm/m·K10 µin/in·°F · Latent Heat of Fusion 150 J/g64.5 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 11.5 % IACS · Electrical Resistivity 1.5×10⁻⁷ Ω·m5.91 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.31 V · Corrosion Resistance 45 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Same in both: Machinability 82 / 100 · Machinability Rating (AISI 1212 = 100 %) 80% · Weldability 8 / 100 · Formability (cold) 5 / 100 · Castability 88 / 100 · Brazeability / Solderability 35 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 40 MJ/kg17,197 BTU/lb · Embodied Carbon (primary production) 2.8 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C93900-M01 vs C93900-M07 — frequently asked
Is C93900-M07 stronger than C93900-M01?
Yes. C93900-M07 has a typical yield strength of 152 MPa (22 ksi) against 138 MPa (20 ksi) for C93900-M01 — about 10% more. Tensile strength is 207 MPa (30 ksi) vs 193 MPa (28 ksi).
Which condition does FabDigit quote by default, M01 or M07?
M07 is the default C93900 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C93900-M01 over C93900-M07?
Pick C93900-M01 when the part is bent, formed or impact-loaded. Pick C93900-M07 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C93900-M01 and C93900-M07 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.